1) high-density polyethylene pipe (HDPE)
高密度聚乙烯管(HDPE)
4) HDPE (High-density polyethylene)
HDPE(高密度聚乙烯)
5) double-wall bellow with higher density polyethylene (HDPE)
高密度聚乙烯(HDPE)双壁波纹管
6) HDPE pipe
高密度聚乙烯管
1.
Combined with concrete survey of project,it illustrates functional features of HDPE pipe,introduces important points & difficult points of project, and discusses main constructive methods from aspects of digging pitch、construction of basic pipe and installation of pipe.
阐述了高密度聚乙烯管的性能特点,结合具体的工程概况,介绍了工程的重点及难点,从沟槽开挖、管道基础施工、管道安装等方面,对主要的施工方法作了探讨。
2.
In this paper the writer compared HDPE pipe with concrete pipe on cost of construction, time limit for a project, hydraulic condition and others, points out that HDPE pipe possesses some advantages such as lighter weight, lower comprehensive cost and shortening time in construction.
通过对高密度聚乙烯管与传统砼管在工程造价、工期、水力条件等方面的比较 ,指出高密度聚乙烯管具有重量轻、综合造价低、施工工期短等优点 ,在市政排水工程中有广阔的应用前
补充资料：高密度聚乙烯（HDPE）塑料的注塑工艺参数
高密度聚乙烯（HDPE）料筒温度 喂料区 30～50℃（50℃） 区1 160～250℃（200℃） 区2 200～300℃（210℃） 区3 220～300℃（230℃） 区4 220～300℃（240℃） 区5 220～300℃（240℃） 喷嘴 220～300℃（240℃）括号内的温度建议作为基本设定值，行程利用率为35％和65％，模件流长与壁厚之比为50：1到100：1 熔料温度 220～280℃ 料筒恒温 220℃ 模具温度 20～60℃ 注射压力 具有很好的流动性能，避免采用过高的注射压力80～140MPa（800～1400bar）；一些薄壁包装容器除外可达到180MPa (1800bar) 保压压力 收缩程度较高，需要长时间对制品进行保压，尺寸精度是关键因素，约为注射压力的30％～60％背压 5～20MPa（50～200bar）；背压太低的地方易造成制品重量和色散不均注射速度 对薄壁包装容器需要高注射速度，中等注射速度往往比较适用于其它类的塑料制品螺杆转速 高螺杆转速（线速度为1.3m/s）是允许的，只要满足冷却时间结束前就完成塑化过程就可以；螺杆的扭矩要求为低计量行程 0.5～4D（最小值～最大值）；4D的计量行程为熔料提供足够长的驻留时间是很重要的残料量 2～8mm，取决于计量行程和螺杆直径回收率 可达到100％回收收缩率 1.2～2.5％；容易扭曲；收缩程度高；24h后不会再收缩（成型后收缩）浇口系统 点式浇口；加热式热流道，保温式热流道，内浇套；横截面面积相对小，对薄截面制品已足够机器停工时段 无需用其它材料进行专门的清洗工作；PE耐温升料筒设备 标准螺杆，标准使用的三段式螺杆；对包装容器类制品，混合段和切变段几何外形特殊（L：D＝25：1），直通喷嘴，止逆阀
说明：补充资料仅用于学习参考，请勿用于其它任何用途。