1) zeolite/ZSM-5 zeolite membrane
沸石/ZSM-5沸石膜
2) ZSM-5 zeolite membrane
ZSM-5沸石膜
1.
Synthesis of high permeability ZSM-5 zeolite membrane by adjusting seed size;
调控晶粒尺寸合成高渗透ZSM-5沸石膜
2.
Hydrothermal stability of ZSM-5 zeolite membrane was investigated under action of water vapor at 400 ℃ for 200 h.
考察了ZSM-5沸石膜在400℃水蒸气处理200 h条件下的水热稳定性,用气体渗透实验、XRD、SEM对水蒸气处理前后的膜管进行了表征,比较了两者的差别。
3.
ZSM-5 zeolite membranes synthesized on rough porous α-Al2O3 tubes with an average pore size of 2μm in the absence of organic template crystallization gel were investigated.
制备的ZSM-5沸石膜H2的渗透率为1。
3) ZSM 5 zeolite membrane
ZSM-5沸石膜
1.
ZSM 5 zeolite membrane on α Al 2O 3 ceramic tube was synthesized.
在α-Al2 O3陶瓷管载体上 ,采用廉价的正丁胺模板剂合成了 ZSM-5沸石膜 ,探讨了成膜的一些影响因素。
4) ZSM-5 zeolite
ZSM-5沸石
1.
Operating conditions of vapour phase transalkylation of benzene with diethylbenzene over ZSM-5 zeolite catalyst;
ZSM-5沸石催化剂上苯与二乙苯气相烷基转移反应条件研究
2.
Coke formation of ZSM-5 zeolite during toluene disproportionation process was investigated in an integral reactor.
采用积分反应器研究了甲苯非临氢歧化反应中ZSM-5沸石催化剂的积碳规律,得到了积碳速率与反应时间的关联式,并考察了不同反应参数对积碳的影响。
3.
Removal of thiophene from coke-oven benzene over the HZSM-5 zeolite was investigated.
结果表明:噻吩在HZSM-5沸石催化剂的作用下被分解生成硫化氢气体逸出,进而达到脱硫的目的。
6) ZSM-5
ZSM-5沸石
1.
The preparation of ZSM-5 and the characterization of their adsorption performance for MTBE research;
ZSM-5沸石的制备及其对甲基叔丁基醚的吸附性能研究
2.
Based on both of liquid-phase and solid-phase transformation mechanism,ZSM-5 zeolite was synthesized in a solid-like system.
结合实验过程对类固相体系合成 ZSM-5沸石的晶化机理进行了初步探索。
补充资料:钢沸石
Na20·Al203·2Si02·nH20
黄绿色、绿灰色或赤褐色天然矿石颗粒。是一种复杂的硅酸盐。密度2.2-2.4g/cm3。 硬度为3.5-5.5。由含水的钠、钙、钡、铝、钾、铝的硅酸盐矿物组成。
应用 主要用于中小锅炉的软水处理,以除去水中的钙、镁离子,使水质软化,锅炉不生锅垢、水锈,保证安全运转。
黄绿色、绿灰色或赤褐色天然矿石颗粒。是一种复杂的硅酸盐。密度2.2-2.4g/cm3。 硬度为3.5-5.5。由含水的钠、钙、钡、铝、钾、铝的硅酸盐矿物组成。
应用 主要用于中小锅炉的软水处理,以除去水中的钙、镁离子,使水质软化,锅炉不生锅垢、水锈,保证安全运转。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。