1) Mo/V
钼钒比
2) color comparison method of ammonium vanadate-molybdate
钒钼酸铵比色法
1.
Phosphorus content in hydroxyapatite is determined by the color comparison method of ammonium vanadate-molybdate.
采用钒钼酸铵比色法测定羟基磷灰石中磷的含量,考察了波长、显色时间、显色剂用量、硝酸溶液的加入量和温度对测定结果的影响。
3) P-V-Mo yellow colorimetric method
磷钒钼黄比色法
1.
Mo-Sb colorimetric method and P-V-Mo yellow colorimetric method were used to determine the content of total phosphorus in different parts of wetland plants,and the difference in determination results obtained by two methods was compared.
利用钼锑抗比色法和磷钒钼黄比色法测定湿地植物不同器官的全磷含量,比较两种测定方法存在的差异。
4) vanadium-ammonium molybdate colorimetry
钒-钼酸铵比色法
5) Vanadium molybdate yellow colorimetric method
钒钼黄比色法
补充资料：钛8铝1钼1钒合金
分子式：
CAS号：
性质：为近α钛合金。成分铝8％，钼、钒各1％，余量钛。加铝稳定α相，加钼、钒稳定β相。室温抗拉强度896MPa，屈服强度827MPa，延伸率10％，杨氏模量2700GPa，冲击韧性20.3～33.9J，疲劳极限565MPa。采用真空自耗电弧炉熔炼。用于制造航天航空用零部件。
CAS号：
性质：为近α钛合金。成分铝8％，钼、钒各1％，余量钛。加铝稳定α相，加钼、钒稳定β相。室温抗拉强度896MPa，屈服强度827MPa，延伸率10％，杨氏模量2700GPa，冲击韧性20.3～33.9J，疲劳极限565MPa。采用真空自耗电弧炉熔炼。用于制造航天航空用零部件。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条