1) Flame Hydrolysis Deposition (FHD)
火焰水解法(FHD)
2) flame hydrolysis deposition
火焰水解法
1.
SiO 2 and GeO 2:SiO 2 films are deposited on silicon substrate by flame hydrolysis deposition (FHD).
采用火焰水解法在Si基上淀积SiO2 /GeO2 :SiO2 预制材料 ,然后在真空中 /空气气氛中高温处理 ( 1380℃ )后 ,制得玻璃化的SiO2 /GeO2 :SiO2 膜材料。
3) flame hydrolysis deposition
火焰水解
1.
GeO_2-and B_2O_3-doped silica optical waveguide materials were prepared on silicon substrate by flame hydrolysis deposition.
用火焰水解法在硅基片上制备了掺杂GeO2和B2O3的SiO2光波导材料。
2.
Thick SiO 2 and B 2O 3-P 2O 5-SiO 2 cladding materials for waveguide are fabricated on single crystal silicon substrate by flame hydrolysis deposition and high-temperature consolidation.
用火焰水解和高温烧结的方法在单晶硅基片上制备了厚SiO2 和B2 O3 P2 O5 SiO2 光波导包层材料。
3.
Germanium doped silica (GeO 2-SiO 2) soot is deposited on single crystal silicon substrate by flame hydrolysis deposition.
用火焰水解法在单晶Si片上沉积了掺Ge的SiO2 (GeO2 SiO2 )粉末 ,随后在高温炉中将此粉末烧结成玻璃 。
4) flame pyrolysis
火焰裂解
补充资料：低压压热釜油脂水解法
分子式：
CAS号：
性质：早期常用的油脂水解工艺方法。油脂和水在压热釜中通入压力为1MPa的饱和蒸汽。温度达到该压力下的饱和温度(约180℃)。由于在此温度下水在油脂中的溶解度不够，要加入碱性催化剂，一般用钙、镁或锌的氧化物，以氧化锌较普遍。其实质是第一步生成上述碱土金属的皂，金属皂使油脂与水形成油包水型乳液。在上述条件下反应时间为10h左右，分批进行，分解率可达95％。当原料质量好时，所得的脂肪酸色泽浅，不经蒸馏即可直接用于制皂或其他产品。
CAS号：
性质：早期常用的油脂水解工艺方法。油脂和水在压热釜中通入压力为1MPa的饱和蒸汽。温度达到该压力下的饱和温度(约180℃)。由于在此温度下水在油脂中的溶解度不够，要加入碱性催化剂，一般用钙、镁或锌的氧化物，以氧化锌较普遍。其实质是第一步生成上述碱土金属的皂，金属皂使油脂与水形成油包水型乳液。在上述条件下反应时间为10h左右，分批进行，分解率可达95％。当原料质量好时，所得的脂肪酸色泽浅，不经蒸馏即可直接用于制皂或其他产品。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条