1) low saturated precipitation
低过饱和沉淀法
1.
Some Zn-A1 hydrotalcites which the molar ratio of Zn to A1 is 2:1 were synthesized respectively by high and low saturated precipitation methods.
分别用高、低过饱和沉淀法合成了n(Zn)/n(Al)=2:1的Zn-Al类水滑石(HTlc),并用XRD对所获得的水滑石样品进行了表征,结果表明:高过饱和沉淀法合成的水滑石的谱峰比低过饱和沉淀法合成的水滑石的谱峰更尖锐,说明高过饱和沉淀法的结晶效果优于低过饱和沉淀法。
2) high saturated precipitation
高过饱和沉淀法
1.
It was found that the high saturated precipitation synthetic hydrotalcite peaks than the low saturated precipitation peaks is more acute.
分别用高、低过饱和沉淀法合成了n(Zn)/n(Al)=2:1的Zn-Al类水滑石(HTlc),并用XRD对所获得的水滑石样品进行了表征,结果表明:高过饱和沉淀法合成的水滑石的谱峰比低过饱和沉淀法合成的水滑石的谱峰更尖锐,说明高过饱和沉淀法的结晶效果优于低过饱和沉淀法。
3) saturated ammonium sulphate
饱和硫酸铵沉淀
4) neutralization precipitation method
中和沉淀法
1.
The dissertation adopted neutralization precipitation method, which used ammonia to neutralize aluminum sulfate solution and aluminum nitrate solution respectively to produce fine aluminum hydroxide powder.
本文采用中和沉淀法,使用氨水分别中和硫酸铝溶液及硝酸铝溶液来制备氢氧化铝粉体。
5) low-temperature coprecipitation method
低温共沉淀法
1.
MnFe_2O_4 nanocrystals were prepared by low-temperature coprecipitation method,high temperature method and hydrothermal method respectively.
本文分别采用低温共沉淀法、高温法和水热法制备MnFe2O4的纳米晶体。
6) chilled alcohol precipitation method
低温乙醇沉淀法
补充资料：低收缩不饱和聚酯树脂
分子式：
CAS号：
性质：含低收缩添加剂(主要是热塑性树脂)的不饱和聚酯树脂。树脂的体积收缩率可由7％～10％缩小至0.2％。常用的低收缩添加剂按其在苯乙烯中的溶解度分为可溶性添加剂，如聚苯乙烯；不溶性添加剂，如聚乙烯、聚丙烯和乳液法生产的聚氯乙烯；溶胀性添加剂，如氯乙烯-醋酸乙烯共聚物其中聚乙烯、聚丙烯和树脂的相容性差，模压流动性欠佳。由低收缩树脂制得的制品，表面光洁、波纹度小，强度好，收缩率低。主要用于制造片状模塑料和团状模塑料，适于模塑精度要求高的结构部件，供电器、汽车、仪表等部门应用。