1) fractal shrinkingcore model
分形缩核模型
2) shrinking core model
缩核模型
1.
A shrinking core model is used to account for the calcination process of ultra-fine limestione.
采用缩核模型对超细石灰石热解进行了模拟。
2.
When the reaction is controlled by the diffusion through liquid,the dissolution process of mono-sized particles was predicted based on the shrinking core model.
当液-固反应为流体扩散控制时,以缩核模型为基础,得到了单颗粒消溶时粒径的变化规律,满足平方反比定律;在单颗粒消溶的基础上,建立了颗粒群消溶模型,得到了单颗粒微观反应模型和颗粒群宏观反应特征的关联关系。
3) nucleation model
形核模型
1.
Based on the statistical analysis of a number of experimental data,a nucleation model was developed and the related thermodynamics and kinetics parameters were presented for low pressure die casting of ZL114A aluminum alloy.
在大最实验数据统计分析的基础上,建立了低压铸造ZL114A铝合金形核模型,得到了相关热力学、动力学参数。
2.
An experiential nucleation model in solidification processes of the industrial alloys was established by introducing the experimental parameters.
为了定量地描述多元合金的实际形核过程,引入实验参数,建立了工业多元合金凝固过程中的经验形核模型,该模型把形核率与最终晶粒密度联系起来。
4) Shrinking core model
收缩核模型
5) contracting core model
收缩核模型
1.
The contracting core model was applied.
结果说明,应用收缩核模型确定扩散是该体系反应的控制步骤,得知在高温下可用Ca主要以气态形式迁移,还原La2O3生成La,La再往Ni中扩散生成LaNi5,同时求得生成LaNi5的表观活化能为33 kJ。
2.
The contracting core model is .
XRD物相鉴定证明生成物是TbFe2 ;应用收缩核模型得知 :扩散是反应的控制步骤 ,表观活化能Ea=39kJ·mol- 1 。
3.
The contracting core model was applied, and it was shown that the diffusion is the rate-determining step of the system.
分析了 Ｃａ－Ｄｙ_２Ｏ_３－Ｆｅ体系高温还原－扩散制备 ＤｙＦｅ_２热力学可能性，应用收缩核模型确定扩散是该体系反应的控制步骤，并进行了ＸＲＤ，ＥＤＸ与ＳＥＭ分析，得知在高温下可用 Ｃａ还原 ＤｙＺＯｓ生成 Ｄｙ； Ｄｙ向 Ｆｅ中扩散生成 ＤｙＦｅ２，同时求得 ＤｙＦｅ_２的表观活化能为２１０ｋＪ／ｍｏｌ。
6) shrink core model
缩小核模型
补充资料：缩核模型
分子式：
CAS号：
性质：反应过程中颗粒不断变小的非催化气-固反应模型。如固体颗粒的燃烧，若反应产物是挥发物，在颗粒上不残留灰层，则在反应过程中颗粒的直径不断变小，最后完全消失。根据这种反应机理建立的颗粒反应数学模型。
CAS号：
性质：反应过程中颗粒不断变小的非催化气-固反应模型。如固体颗粒的燃烧，若反应产物是挥发物，在颗粒上不残留灰层，则在反应过程中颗粒的直径不断变小，最后完全消失。根据这种反应机理建立的颗粒反应数学模型。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。