1) surface composite layer
表面复合层
1.
By optimizing the electron beam parameters, chromium carbide is in situ synthesized in the surface composite layer.
通过电子束加热工艺和粉末配比的优化,在表面复合层中原位合成了(Cr,Fe)7C3。
2.
By optimizing the electron beam parameters,chromium carbide is in-situ synthesized in the surface composite layer.
以Fe/Cr/C粉末为添加粉末,通过电子束加热工艺参数的优化,在表面复合层中原位合成了碳化铬。
2) composite plating surface
复合镀层表面
1.
A new method of Ni-PTFE composite plating surface used as promoter of dropwise condensation of water vapor was investigated.
研究了采用Ｎｉ－ＰＴＦＥ复合镀层表面实现水蒸气滴状冷凝的新方法。
3) composite external coats
复合表面涂层
4) Al2O3/Cu compound layer
Al2O3/Cu表面复合层
1.
Al2O3/Cu compound layer was prepared through internal oxidation of aluminized copper.
利用纯铜渗铝-内氧化工艺制备了Al2O3/Cu表面复合层,测试了表层的组织结构和力学性能,并进行了黏着磨损、固定磨料磨损和松散磨料振动与非振动情况下的磨损试验。
5) vanadium-Chromium composite layer
钒铬表面复合层
6) Al2O3/Cu composites layer
A12O3/Cu表面复合层
1.
Influence of the aluminum in aluminizing agents on the aluminum distribution in the copper surface is discussed, the microstructure and properties of Al2O3/Cu composites layer under different technical parameter are studied.
本文采用包埋法纯铜渗铝-内氧化工艺制备A12O3/Cu表面复合层,考察了渗剂中铝含量对表面渗层中铝含量分布的影响,并对采用不同工艺参数条件下获得的A12O3/Cu表面复合层的显微组织和性能进行了相关研究。