1) bulk ultrafine grained materials
块体超细晶材料
1.
The severe plastic deformation(SPD) is an effective route to full-density bulk ultrafine grained materials(UFG) free of porosity and contamination.
强烈塑性变形是一种获得无孔洞、无界面污染且致密块体超细晶材料的有效途径。
2) bulk ultrafine-grained and nanocrystalline materials
块体纳米/超细晶材料
3) ultra-fine grained material
超细晶材料
1.
The research development of ultra-fine grained material process by ECAP is summarized, and the technical principle and process character of ECAP are introduced, as well as the effect on microstructure of ECAP fine grained material caused by ECAP die is mainly analyzed, and ECAP die structure is optimized.
论述了等径角挤压(ECAP)制备超细晶材料工艺的研究进展,介绍了ECAP的技术原理和工艺特点,着重分析了ECAP模具对ECAP细晶材料的显微组织的影响,优化ECAP模具结构。
5) ultrafine-grained material
超细晶材料
1.
Equal channel angular pressing (ECAP) is currently focused due to its capability to fabricate bulk ultrafine-grained material.
等径弯曲通道变形(Equal ChannelAngularPressing简称ECAP)由于能直接制备块状超细晶材料而备受关注。
6) ultra-fine grain material
超细晶材料
1.
The compression-torsion forming technology has been used in preparing ultra-fine grain material.
采用高压扭转方法可以制备超细晶材料,在坯料高度方向施加压力的同时,沿坯料横截面方向施加扭矩,达到大塑性变形产生超细晶。
补充资料：超细纤维驻极体毡
分子式：
CAS号：
性质：又称带电超细纤维毡，由熔喷法超细纤维毡经电晕等处理而具有长期稳定的电荷和高表面电荷密度，以提高过滤效率。基本上各种热塑性聚合物都可用，以平均直径3μm、定积重量40g/m2的聚丙烯超细纤维驻极体毡为例，分极电荷量为7.2×10-10C/cm2，过滤效率99.998％。制法是在熔喷时施加约10kV/cm的电压，聚丙烯毡的表面温度40℃，分极电荷高峰温度各为92℃和152℃时，活化能各为0.35和0.62电子伏特(eV)。用途为高性能滤材、吸附材料、高效口罩、防护衣、被褥、座垫等。
CAS号：
性质：又称带电超细纤维毡，由熔喷法超细纤维毡经电晕等处理而具有长期稳定的电荷和高表面电荷密度，以提高过滤效率。基本上各种热塑性聚合物都可用，以平均直径3μm、定积重量40g/m2的聚丙烯超细纤维驻极体毡为例，分极电荷量为7.2×10-10C/cm2，过滤效率99.998％。制法是在熔喷时施加约10kV/cm的电压，聚丙烯毡的表面温度40℃，分极电荷高峰温度各为92℃和152℃时，活化能各为0.35和0.62电子伏特(eV)。用途为高性能滤材、吸附材料、高效口罩、防护衣、被褥、座垫等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条