1) cyclocarbonates
环化碳酸酯
2) cyclocarbonate
环碳酸酯
1.
Study on synthesis and characterization of cyclocarbonate;
多元环碳酸酯的合成与表征
2.
Nonisocyanate polyurethane(NIPU) was synthesized by aliphatic primary diamine and cyclocarbonate prepared from epoxy resin E-44.
以环氧树脂E-44为原料合成了环碳酸酯,再与脂肪族伯胺反应合成了非异氰酸酯聚氨酯。
3.
The recent research progress in nonisocyanate polyurethane(NIPU) prepared by cyclocarbonate-and amino-oligomer and synthetic mechanism wherein were reviewed in this paper.
综述了非异氰酸酯聚氨酯(NIPU)及其两种合成原料环碳酸酯齐聚物和胺类齐聚物的最新研究进展,讨论了环碳酸酯和胺类齐聚物的合成方法以及NIPU的合成机理,介绍了NIPU的应用范围、发展前景及国外企业对于此类新型材料的最新研发情况和工业动态。
3) cyclic carbonate
环碳酸酯
1.
The results demonstrated that the coupling reaction of CO2 and epoxides to form cyclic carbonates with high yield proceeds very effectively at 413 K under 1.
0 MPa条件下,以溴化锌为催化剂,苯基三甲基三溴化铵为共催化剂,无需加入任何溶剂就可以使二氧化碳和环氧化合物发生偶联反应,并以很高的收率得到环碳酸酯。
2.
New generation polyurethane, nonisocyanate polyurethane(NIPU),which shows lower permeability,higher chemical resistance and non-poisonous fabrication process compared with traditional polyurethane,is obtained from multifunctional cyclic carbonates and multifunctional primary polyamines.
由多环碳酸酯和多元胺合成而来的非异氰酸酯聚氨酯有望成为一种性能良好的绿色环保材料替代传统聚氨酯。
3.
Finally, cyclic carbonate-terminated polyether (CCP) with flexible backbone was synthesized using ETP as the raw material.
最后,本文以ETP为原料,合成了具有柔顺主链的端环碳酸酯基聚醚(CCP)。
4) polyester carbonate cyclocompound
聚酯碳酸酯环化合物
5) Dicyclohexyl peroxydicarbonate
过氧化二碳酸二环己酯
6) polysulfone carbonate cyclocompound
聚砜碳酸酯环化物
补充资料：硫代碳酸酯-碳酸酯共聚物
分子式：
CAS号：
性质：分子主链同时含有碳酸酯和硫代碳酸酯重复结构单元的共聚物。其结构式为:具有水解稳定性优良的特点。热变形温度(1.82MPa)159～168℃：拉伸强度58.61MPa，冲击强度15.2kJ/m2；介电常数(105Hz)2.69～3.01；成型温度220～235℃。在光气中加入部分硫代光气后与双酚A进行界面缩聚反应制得。可在电子、电器、仪表等行业用作耐热绝缘制品。
CAS号：
性质：分子主链同时含有碳酸酯和硫代碳酸酯重复结构单元的共聚物。其结构式为:具有水解稳定性优良的特点。热变形温度(1.82MPa)159～168℃：拉伸强度58.61MPa，冲击强度15.2kJ/m2；介电常数(105Hz)2.69～3.01；成型温度220～235℃。在光气中加入部分硫代光气后与双酚A进行界面缩聚反应制得。可在电子、电器、仪表等行业用作耐热绝缘制品。