1) blend-weaving
混织
1.
The composite sheets were fabricated from cospinning or blend-weaving textiles of modified ramie fibers and polymer in hot-pressing.
本文将改性的苎麻与树脂混纺或混织的织物在热压机上压制成苎麻纤维与树脂的复合板材。
2) blended fabric
混纺织物
1.
Pretreatment of PLA/cotton blended fabric;
聚乳酸/棉混纺织物的前处理
2.
Union dyeing of chitin/cotton blended fabric;
甲壳素/棉混纺织物匀染性改进
3.
Development of wool type bamboo fiber/long ramie fiber blended fabric;
毛型竹浆纤维/苎麻长纤维混纺织物的开发
3) blended fabrics
混纺织物
1.
Study on the balling up of fine denier polyester blended fabrics;
细旦涤纶混纺织物抗起毛起球性能研究
2.
Design and wet processing of polyester/linen blended fabrics
涤/麻混纺织物的设计及染整工艺
3.
and time in the anti-crease finishing, and the optimum process was found for ramie blended fabrics according to the strength loss and elastic recovery angles (T+W).
对影响整理效果的树脂和催化剂用量、焙烘温度和时间等因素进行了试验,以强力损失和弹性回复角(T+W)指标为依据,找出了适合苎麻棉混纺织物抗皱整理的最佳工艺:树脂NDW100g/L、催化剂MgCl220g/L、纤维保护剂SVN20g/L,焙烘温度160℃,焙烘时间控制在3min,弹性回复角(T+W)可达265°,强力损失38。
5) mixed microstructures
混晶组织
1.
It shows that the surface crack of steel wire rod and mixed microstructures are main cause for drawing fracture.
保证钢坯表面完整,如有缺陷应予以铲除,不合格钢坯严禁入炉,可避免盘条表面裂纹;加热温度过高形成的混晶组织可通过选择1000~1050℃加热来解决;适当提高加热温度可避免在轧制前出现混晶;吐丝温度设定950~980℃有利于得到易于拉拔的均匀细小晶粒组织。
6) silk and linen interlacing
丝/麻混织
补充资料：混头混脑
1.头脑胡涂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。