1) cold stamping female die
冷压凹模
1.
The fracture analysis result of the failure cold stamping female die shows that the little crack of the cold stamping die belongs to fatigue crack,and that at the same time the non-uniform distribution of the carbide can introduce the crack origination and the low-cycle fatigue rupture failure of die.
由冷压凹模断口形貌失效分析结果表明,凹模内壁微小裂纹属于疲劳裂纹,同时凹模材质CrWMn钢中的所存在的碳化物不均匀性诱发了裂纹的产生,导致模具在低周疲劳状态下发生断裂失效。
2) cold extrusion concave die
冷挤压凹模
1.
Optimum design of multi-layer press-fit composite cold extrusion concave die;
多层压配组合冷挤压凹模的优化设计
2.
It is well known that the rational design of multi layer press fit composite cold extrusion concave die is an effective method of increasing the load capacity, extending the life, and saving the material of a cold extrusion concave die.
采用疲劳强度设计理论和最优化设计理论相结合的方式探讨多层压配组合冷挤压凹模的更为合理、有效的设计方法 。
3) cold punch cavity die
冷冲凹模
1.
The crack arrest in Cr12 cold punch cavity die with half-embedding and half-ellipse crack on inside surface using electromagnetic heating was analyzed.
对内表面含有半埋藏半椭圆裂纹的Cr12冷冲凹模进行了电磁热止裂研究。
4) cold embossing
冷压(凹凸)印
5) stamping cavity die
冲压凹模
6) rib-pressing die
压筋凹模
补充资料：凹模壁厚及凹模垫板尺寸
型腔壁部投影面积 壁 厚， 毫 米
F， 厘米2 h1 h2 h3 h4 h5
<5 15~20 30~40 <=10 15~20 30~40
>5~10 20~25 40~50 10~15 20~25 40~55
>10~50 20~30 50~60 15~20 20~30 55~65
>50~100 30~35 60~75 20~25 30~40 65~70
>100~200 35~40 75~85 25~30 40~50 70~75
>200 >40 >85 30~35 50~60 >80
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条