1) Fused ceramite
电熔陶粒砂
2) fused magnesia
电熔镁砂
1.
By using fused magnesia and sintered spinel as main materials and sulphite liquor as binders,magnesium compound side gate was researched.
以优质电熔镁砂、烧结镁铝尖晶石为主要原料,采用纸浆废液作为结合剂研究镁质复合滑板材料。
2.
MgO-ZrO2 samples were prepared by fused magnesia and zircon.
以电熔镁砂和锆英石为原料,研究锆英石质量分数和烧成温度对镁锆质试样物理性能的影响,利用X射线衍射、扫描电镜及能谱分析等手段对试样的物相组成和显微结构进行分析。
3.
In this paper, effect of properties of advanced magnesite-chrome brick on fine powder turning very small, the chromium concentrate powder and fused magnesia powder content, the amount of Zirconium dioxide to be studied identified RH furnace quality magnesite-chrome brick in the best process technique.
本文主要研究了细粉微细化、铬精矿细磨、电熔镁砂粉的含量和ZrO_2的加入量对再结合镁铬砖性能的影响,确定了RH炉用优质镁铬砖的最佳生产工艺。
3) Fused magnesite
电熔镁砂
1.
The effect of additions on properties of the dry magnesite refractory was investigated with fused magnesite as main raw materials,microsilica and sintering promoter as additions.
以电熔镁砂为主要原料,研究了添加剂二氧化硅微粉和烧结剂加入量对镁质干式料性能的影响。
2.
The raw material is made up of fused magnesite particles(particle size 0 to 3 mm),fine fused magnesite powder with the size less than 200 meshes and fine fused magnesia-zirconia s powder with the size less than 320 meshes,polyvinyl alcohol and calcium lignosulfonate liquor being used as the combine.
以0~3mm的电熔镁砂颗粒、<200目的电熔镁砂粉、<320目的电熔共晶镁锆粉为原料,以聚乙烯醇和木质素磺酸钙的溶液为结合剂,研究烧结温度、保温时间对制品烧结性能的影响。
4) quartz sand and ceramisite
石英砂和陶粒
1.
A mass of testing data demonstrated that water purification performance of double layered quartz sand and ceramisite is obviously better than double layered quartz sand and anthracite or single layered quartz sand filtering materials.
大量的试验数据表明石英砂和陶粒组成的双层滤料,其净水处理性能明显好于石英砂和无烟煤双层滤料以及单层石英砂滤料,特别是出水浊度、微絮凝作用,反冲洗周期、藻类的去除、絮凝剂的使用量等指标上具有明显优势,陶粒做为一种新的水处理滤料,正被应用于净水和污水处理。
5) fused magnesia-chrome
电熔镁铬砂
6) fused MgO-ZrO2 eutectic powder
电熔MgO-ZrO2共晶砂
1.
The effect of 10%,15% and 20% progressive addition of fused MgO-ZrO2 eutectic powders to replace magnesia is investigated.
在以电熔镁砂、鳞片石墨为原料、酚醛树脂为结合剂的低碳MgO-C砖中,分别添加10%,15%,20%的电熔MgO-ZrO2共晶砂替代镁砂,经200,1000,1500℃处理后,对材料的体积密度、显气孔率、耐压强度、线变化率、热膨胀率和抗氧化性进行了检测,并借助XRD研究了试样的物相组成和显微结构。
补充资料：电熔β-氧化铝砖
分子式：
CAS号：
性质：又称电熔β-氧化铝砖或熔铸β-刚玉砖。用工业氧化铝作为原料、用工业氧化铝作为原料、β-Al2O3为主晶相的熔铸耐火材料。氧化铝含量约为95%，其他氧化物约含5%（一般是Na2O）。矿物级忝中β-Al2O3约占99%（β-Al2O3是一种假定式为Na2O·11Al2O3的多铝酸盐，或者通式为RO·6Al2O3的钙、钡、锶的铝酸盐），以较大的板状结晶互相啮合，玻璃相较少。熔铸β-Al2O3砖对碱蒸气呈惰性，在不含碱的气氛中易分离出碱而转化为α-Al2O3，并因伴有体积收缩而引起砖的碎裂。这种砖耐热震性较好，从700℃到常温，在空气中可循环40次左右。这种砖一般用于砌筑玻璃熔池的上部结构。
CAS号：
性质：又称电熔β-氧化铝砖或熔铸β-刚玉砖。用工业氧化铝作为原料、用工业氧化铝作为原料、β-Al2O3为主晶相的熔铸耐火材料。氧化铝含量约为95%，其他氧化物约含5%（一般是Na2O）。矿物级忝中β-Al2O3约占99%（β-Al2O3是一种假定式为Na2O·11Al2O3的多铝酸盐，或者通式为RO·6Al2O3的钙、钡、锶的铝酸盐），以较大的板状结晶互相啮合，玻璃相较少。熔铸β-Al2O3砖对碱蒸气呈惰性，在不含碱的气氛中易分离出碱而转化为α-Al2O3，并因伴有体积收缩而引起砖的碎裂。这种砖耐热震性较好，从700℃到常温，在空气中可循环40次左右。这种砖一般用于砌筑玻璃熔池的上部结构。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条