1) TiNi alloy sheet
薄片状TiNi合金
2) TiNi(Cu) shape memory alloy thin films
TiNi(Cu)形状记忆合金薄膜
3) TiNi shape memory alloy film
TiNi形状记忆合金薄膜
1.
In this work, TiNi shape memory alloy films on oxidized single crystal Si substrate were successfully prepared by co-sputtering of TiNi target with a separated Ti target.
利用磁控溅射的方法在氧化后的单晶Si基片上制备了TiNi形状记忆合金薄膜,利用示差扫描量热法和原位X射线衍射研究了薄膜的马氏体相变特征。
4) TiNi alloy thin film
TiNi合金薄膜
1.
The paper mainly study the preparation process of the near or same atomic proportion TiNi alloy thin film and the shape transformation of TiNi alloy thin film at dynamic heating and cooling condition,disclosure the transmutation process of TiNi alloy thin film from austenite to martensite.
本论文主要研究近等原子比TiNi合金薄膜的制备工艺以及TiNi合金薄膜在动态加热、冷却过程所发生的相变,揭示了TiNi合金薄膜从奥氏体到马氏体的演变过程。
5) TiNi thin cylindrical shells
TiNi合金薄柱壳
6) TiNi SMA
TiNi形状记忆合金
1.
Influence of Brazing Temperature on the Properties and Microstructure of TiNi SMA;
钎焊温度对TiNi形状记忆合金性能和组织的影响
补充资料：铝合金的羽毛状晶
铝合金的羽毛状晶
feathey crystal of aluminium alloy
IUheJ旧deyumooZhuangJ旧g铝合金的羽毛状晶(feathey Crystal of alu-minium anoy)铝合金铸锭中柱状晶的变种，形状类似羽毛的晶粒。是铸锭缺陷的一种。形状近似直线状花边的羽毛状晶亦称为“花边状组织”。羽毛状晶成群出现，每群中羽毛状晶之间近似平行。羽毛状晶是双晶，以(111)晶面为双晶面。铝一镁系合金中的羽毛状晶如图所示。’ 产生羽毛状晶的工艺因素主要是:(1)熔体处于高温平稳状态，有较好的定向结晶条件。(2)在铸造温度下熔体停留时间过长，熔体过热和高度净化，减少结晶前沿形成晶核的数量。(3)合金中加入某些容易产生羽毛状晶的微量元素，如硼和错。 超硬铝合金、工业纯铝和高镁铝合金形成羽毛状晶的几率较大，而高强锻造铝合金2A70(LD7)、防锈铝合金 3A21(LF21)和含镁低于5%的铝镁系合金，基本上不形成羽毛状晶。 铸锭中存在羽毛状晶对其性能影响较大。在塑性加工过程中易在羽毛状晶的双晶面处产生裂纹。制品中残留的未完全破碎的羽毛状晶区会扩大使用性能的各向异性。蘸: 铝一镁系合金铸锭中的羽毛状晶偏光只100 (格长清)