1) dropwise segregation
滴状偏析
1.
Causes of dropwise segregation formation are analyzed through observation of morphology of crystallization structures of heavy rail stock.
通过对重轨钢初轧坯结晶组织形态的观察，分析了滴状偏析的成因，结果表明：滴状偏析的形成，是因为浇注温度低，过于粘稠，使富集溶质元素的偏析液不能充分上浮所致。
2) punctum segregation
点状偏析
3) lamellar segregation
层状偏析
1.
In addition, electromagnetic Stirring reduced the lamellar segregation of deposited metals and the composition distribution tended to be homogenous.
电磁搅拌使管线钢埋弧焊缝的层状偏析现象明显改善，成分分布趋于均匀，有利于提高焊缝金属的抗腐蚀性。
4) cellular segregation
网状偏析
5) zonal segregation
带状偏析
1.
The results show that the main reasons of the cracking were the thick,big and large amount of zonal segregation and large nonmetallic inclusions which were distributed in rolling direction of the materials during the quench hardening.
结果表明:原材料组织中的带状偏析和沿轧制方向分布数量多且粗大的非金属夹杂物是弹簧淬火开裂的主要原因;夹杂物和带状偏析造成材料组织和性能均匀性变差,粗大的非金属夹杂物成为裂纹源,在组织应力的作用下,促进裂纹形成并迅速扩展成为沿轧制方向分布的淬火裂纹。
6) segregation and band
偏析和带状
1.
Based on analyzing mass production data, it is found that segregation and bands in 16Mn steel is caused by higher Mn content in the steel.
在分析大生产数据基础上,结合16Mn钢生产质量问题,提出该钢组织偏析和带状严重是与锰含量偏高密切相关的,上述问题可通过控制终轧温度和降低锰含量约20%得以解决并因此获巨大的经济效益。
补充资料：无柄液滴法、躺滴法、座滴法等
分子式：
CAS号：
性质：又称无柄液滴法、躺滴法、座滴法等。根据液面外形求算表(界)面张力的一种方法。当待测液液滴稳定地停在水平固体表面上，其外形与液体表面张力γ有关。根据巴什弗思–亚当斯(Bashforth-Adams)方程可有以下关系式ρ1和ρ2分别为待测液体及液滴外介质的密度，g为重力加速度，β为形状因子，b为大小因子。当液体与固体表面接触角大于90°时可根据测出的液滴的赤道半径及其与液滴顶点的垂直距离数值查表得出相应的β及b值，从而算出表面张力γ。本法简便，适用于吸附平衡时间长的体系和低表面张力的测定；也能用于测定界面张力及熔融金属的表(界)面张力。
CAS号：
性质：又称无柄液滴法、躺滴法、座滴法等。根据液面外形求算表(界)面张力的一种方法。当待测液液滴稳定地停在水平固体表面上，其外形与液体表面张力γ有关。根据巴什弗思–亚当斯(Bashforth-Adams)方程可有以下关系式ρ1和ρ2分别为待测液体及液滴外介质的密度，g为重力加速度，β为形状因子，b为大小因子。当液体与固体表面接触角大于90°时可根据测出的液滴的赤道半径及其与液滴顶点的垂直距离数值查表得出相应的β及b值，从而算出表面张力γ。本法简便，适用于吸附平衡时间长的体系和低表面张力的测定；也能用于测定界面张力及熔融金属的表(界)面张力。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条