1) Pt/WO3 thin film
Pt-WO3薄膜
2) Pt/WO3 nano-film
Pt/WO3纳米薄膜
1.
The constructure and the properties of the Pt/WO3 nano-film were investigated.
研究了该Pt/WO3纳米薄膜的结构和氢敏性能,结果表明,用此种方法制备的WO3基掺Pt薄膜具有良好的氢敏特性;平均膜厚160nm;薄膜经400℃以下退火处理后是非晶态结构,表面疏松多孔,氢敏效果好;经400℃以上退火处理后呈晶态结构,表面粗糙致密,氢敏效果差;Pt掺杂量对薄膜的氢敏效果有影响,掺杂量越多,氢敏效果越差。
3) WO3-TiO2 film
WO3-TiO2薄膜
4) WO_3 thin film
WO3薄膜
1.
The electrochemistry impedance spectroscopies of ITO plane electrodes and ITO plane electrodes with WO_3 thin film immersed in 1 mol LiClO_4 propylene carbonate electrolyte have been studied by means of the surface process Faraday immittance expression and equivalent circuits.
采用表面过程法拉第阻纳表达式方法与等效电路方法,研究透明ITO平面电极及带WO3薄膜层的ITO平面电极处于1 mol LiClO4丙烯碳酸酯电解液中的电化学阻抗谱。
5) WO3 film
WO3薄膜
1.
Nano-WO3 film is the better optical gas sensor material.
WO3薄膜是良好的光学气敏传感器材料。
6) WO3/TiO2 thin film
WO3/TiO2薄膜
1.
In this article,photocatalytic degradation of acid red B(ARB) in aqueous solution was studied with a photocatalytic glass reactor which made of the glass beads evenly coated with transparent WO3/TiO2 thin film by the sol-gel process.
采用溶胶-凝胶法,在玻璃珠表面涂覆均匀透明的WO3/TiO2薄膜,并制成光催化反应器对水溶液中酸性红B(ARB)的光催化降解进行了研究。
补充资料：(beta-4)-tungstate (wo42-calcium
CAS：7790-75-2
分子式：CaO4W
中文名称：钨酸,钙白矿
英文名称：calcium tungstate；( beta-4)-tungstate (wo42-calcium ；calcium tetrahydrogen diphosphate monhydrate
分子式：CaO4W
中文名称：钨酸,钙白矿
英文名称：calcium tungstate；( beta-4)-tungstate (wo42-calcium ；calcium tetrahydrogen diphosphate monhydrate
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条