1) C/C-TaC composites
C/C-TaC复合材料
1.
The microstructures and mechanical properties of C/C-TaC composites were investigated.
采用化学气相渗透(CVI)法和热固性树脂浸渍-炭化法复合工艺制备含5%TaC的新型C/C-TaC复合材料,并对复合材料的微观结构和力学性能进行了研究。
2) C/TaC/C composites
C/TaC/C复合材料
1.
According to the physicochemical properties of C/C composites and TaC and the environment, in which C/TaC/C composites is ablated, the ablation mechanism of C/TaC/C composites is deduced.
根据TaC和C/C复合材料的物理化学性质及烧蚀环境推测C/TaC/C复合材料的烧蚀机理,并对其抗侵蚀机理及剥蚀进行了预测分析,在分析C/TaC/C复合材料烧蚀机理的基础上建立其烧蚀模型。
3) C/C-TaC multi-phase composite material
C/C-TaC多元复合材料
4) carbon/carbon composites
C/C复合材料
1.
Effect of Si/Mo ratio on microstructure and high-temperature antioxidation property of SiC-MoSi_2 coating for carbon/carbon composites;
硅钼含量对C/C复合材料SiC-MoSi_2涂层结构和高温抗氧化性能的影响
2.
The ablation performances of two kinds of carbon/carbon composites with different pyrocarbon were investigated on a high-pressure arc heater.
采用电弧驻点烧蚀试验方法测试了具有典型光滑层和粗糙层热解炭结构的两种C/C复合材料的烧蚀率,研究了热解炭结构对C/C复合材料烧蚀性能的影响。
3.
The advantage of carbon/carbon composites is constrained by its oxidation at high temperature.
C/C复合材料高温氧化性限制了其在高温领域的更广泛应用。
5) C/C composites
C/C复合材料
1.
Ablation characteristics of 2D-C/C composites and their graphitized products;
2D-C/C复合材料及其石墨化制品烧蚀特性分析
2.
Effects of graphitization degree and fiber content on properties of C/C composites;
石墨化度及纤维含量对C/C复合材料性能的影响
3.
Effect of content and type of matrix carbon on sliding tribology behavior of C/C composites;
基体炭含量对C/C复合材料滑动摩擦磨损行为的影响
6) 2D-C/C composite
2D-C/C复合材料
1.
Kinetic model and mechanisms of oxidation of 2D-C/C composite;
2D-C/C复合材料氧化动力学模型及其氧化机理
补充资料：TAC
分子式：
CAS号：
性质：又称三聚氰酸三烯丙酯。熔点31℃。沸点140℃（67Pa）。密度1.1133g/cm3（30℃）。1.5049。对湿气敏感，入口有毒。由氰尿酰氯与烯丙醇在碱催化作用下反应制得。作为交联剂和固化剂用于PMMA、聚烯烃等可可提高其热、氧稳定性和机械强度。
CAS号：
性质：又称三聚氰酸三烯丙酯。熔点31℃。沸点140℃（67Pa）。密度1.1133g/cm3（30℃）。1.5049。对湿气敏感，入口有毒。由氰尿酰氯与烯丙醇在碱催化作用下反应制得。作为交联剂和固化剂用于PMMA、聚烯烃等可可提高其热、氧稳定性和机械强度。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条