1) Ti-V-based alloys
钛钒基合金
1.
Based on a overall review of the research and development of the Ti-V-based hydrogen storage electrode alloys, and the degradation mechanism of the hydrogen storage alloy electrodes, the Ti-V-based alloys were selected as the study objects of this thesis.
在此基础上，确定以钛钒基贮氢电极合金为研究对象，采用XRD／Rietveld、SEM、TEM和AES等材料分析方法以及恒电流充放电、电化学阻抗谱、线性极化、阳极极化和恒电位阶跃等电化学测试技术，对钛钒基合金的成分、相结构与电化学性能三者之间的关系进行了系统的研究，提出贮氢电极合金的“本征／非本征衰退机理”，并以钛钒基合金为实例对该机理进行了验证。
2) TiVCr based alloys
钛钒铬基合金
1.
The influence of suction cast on phase structures and hydrogen storage properties of TiVCr based alloys has been investigated in this work.
研究了吸铸对钛钒铬基合金结构和贮氢性能的影响。
3) Ti-V-Fe-based alloys
钛钒铁基合金
4) TiV alloy
钛钒合金
5) titanium-aluminium-vanadium alloy
钛铝钒合金
6) TiV-based hydrogen storage electrode alloy
钛钒基储氢电极合金
1.
Study on TiV-based hydrogen storage electrode alloy;
钛钒基储氢电极合金研究
补充资料：钛13钒11铬3铝合金
分子式：
CAS号：
性质：β钛合金。成分为钒13％，铬11％，铝3％，余量钛。退火后室温机械性能：抗拉强度862MPa，屈服强度827MPa，延伸率10％，弹性模量10.34×104MPa，HRC硬度32～36。采用真空自耗电弧炉熔炼制取。制造紧固件和较大面积的模锻件。
CAS号：
性质：β钛合金。成分为钒13％，铬11％，铝3％，余量钛。退火后室温机械性能：抗拉强度862MPa，屈服强度827MPa，延伸率10％，弹性模量10.34×104MPa，HRC硬度32～36。采用真空自耗电弧炉熔炼制取。制造紧固件和较大面积的模锻件。