1) mesophase-derived carbon materials
中间相炭材料
2) mesoporous carbon materials
中孔炭材料
1.
Template synthesis and performance of ordered mesoporous carbon materials;
模板法制备有序中孔炭材料及其性能
2.
The mesoporous carbon materials with different specific surface areas was prepared using SBA-15 as a template and sucrose as a carbon source under different carbonized temperatures.
以SBA-15为模板,蔗糖为炭源,在不同的炭化温度下合成了不同比表面积的中孔炭材料。
3) Carbonaceous mesophase
炭质中间相
1.
Carbonaceous mesophase is an excellent precursor for carbon materials,especially those with high additional value.
炭质中间相是制备炭材料,尤其是高附加值炭材料的优质前驱体。
2.
The paper discussed systematically the formation process of carbonaceous mesophase ( CM) by analyzing the explanations in previous papers.
为了分析和预测一定条件下获得的炭质中间相产品的性能、进而确定其具体的用途,需要弄清炭质中间相的形成机理。
4) intermediate material
中间材料
1.
Conclusion\ While the intermediate material is inserted, Ly12 alumini.
方法 针对 Ly1 2铝合金与 A3钢在直接结合的实验中出现的问题进行了详细的分析研究 ,提出了在 Ly1 2铝合金 (覆板 )和 A3钢 (基板 )之间插入中间材料 ( A3钢薄板 )的新的实验方法 。
5) MCMB
中间相炭微球
1.
Research on Preparation and Formation Mechanism of MCMB;
中间相炭微球制备与形成机理的研究
2.
Effects of pre-oxidation and the temperature of heat treatment on composition and microstructure of MCMB
预氧化及热处理温度对中间相炭微球组成和结构的影响
3.
The carbon/graphite molding blocks with high density and strength were prepared from mesocarbon microbeads (MCMB) molded at 100 MPa and then heat-treated.
以中间相炭微球(MCMB)为原料,在100MPa的压力下冷模压成型后,再经过热处理得到高密高强炭/石墨材料。
补充资料：中间相
合金相图中在中间成分区域内形成的均质相。晶体结构一般和组元金属不同,物理、化学和力学性质也迥异。中间相是一类重要的合金相。按照结合键的类型，中间相可以分为离子化合物、共价化合物和金属化合物；按照它们的形成规律和结构、性能特征,又可区分为正常价化合物、电子化合物、 间隙化合物和拓扑密堆相（TCP相）。这些化合物一般具有金属性质,只一部分正常价化合物例外。习惯上中间相又常被称为金属间化合物(in-termetallic compound)。但也有人把成分范围较宽的中间相区分为Ⅱ类固溶体(secondary solid solution)，而用金属间化合物一词专指均质范围比较狭窄，化学计量比较简单的中间相（见合金相）。