1) vacuum infiltration casting
负压渗流铸造
1.
In this paper, ZA alloy has been selected as the base material and ZA alloy foam has been prepared by vacuum infiltration casting process.
因此,本文采用自行设计的负压渗流设备装置,运用负压渗流铸造法成功地制备出了通孔泡沫锌铝合金,对影响泡沫锌铝合金渗流长度的因素进行了研究。
2) upper-pressure infiltration foundry
上压渗流铸造
1.
Technological study on upper-pressure infiltration foundry of porous Co-Cr-Mo alloy;
多孔钴铬钼合金的上压渗流铸造工艺研究
2.
The fusible inorganic material and upper-pressure infiltration foundry technology were used to produce reticular Co-Cr-Mo alloy, the technical parameters of this method were studied in this paper.
利用快速成型技术制得拟替换的骨骼的网状原型,再利用自行筛选的可溶性无机材料及上压渗流铸造工艺来制备网状钴铬钼合金,探讨其制备的工艺参数。
3) pressure penetrating casting
加压渗流铸造
1.
Alsalt composite was fabricated with pressure penetrating casting.
采用加压渗流铸造法制备了铝合金－盐颗粒复合体。
4) Upper-pressure seeping method
上压渗流铸造法
5) vacuum infiltration
负压铸渗
1.
Slurry pump components are prepared by sand mold vacuum infiltration technique.
分别用低铬铸铁、铸造碳钢、灰口铸铁作为基材,采用负压铸渗工艺制造了wc陶瓷颗粒增强表面复合材料渣浆泵泵壳,研究分析其宏观结构和显微组织,优化选择适用于渣浆泵过流件的wc颗粒增强表面复合材料的基材。
2.
The relations between infiltration depth of metal liquid to the capillary between particles and processing parameter have been derived by mathematic analysis for the vacuum infiltration process,i.
通过对负压铸渗理论的分析，得出了影响负压铸渗深度的因素及其影响规律（见式（９））；用碳化钨、镍包氧化铝及不同粒度氧化铝为陶瓷颗粒、耐热钢为基体进行了负压铸渗实验，得到了颗粒分布均匀的复合材料，揭示和证实了颗粒与金属液间的湿润特性及颗粒粒度对铸渗的影响规律。
3.
The high-Cr white cast iron(WCI) matrix composite reinforced with recovered cemented carbide(CC) particles was prepared by the vacuum infiltration casting process.
以回收的钨钴钛类硬质合金为增强颗粒,采用负压铸渗工艺制备了颗粒增强高铬铸铁基复合材料,并借助于金相分析和X射线衍射等手段研究了复合材料的微观界面。
6) penetrating casting
渗流铸造
1.
Study on the technology of penetrating casting for aluminium foam;
泡沫铝合金的渗流铸造工艺方法研究
2.
Elaboration of ZL104 Porous Al Alloy by Means of Penetrating Casting;
渗流铸造法制备ZL104泡沫铝合金
3.
This paper studies penetrating casting process of aluminium foam by orthogonal experiment,analyzes the effect of preheat temperature,casting temperature of granules and forming pressure technical factors on metal liquor forming process.
用正交试验法则研究了泡沫铝的渗流铸造工艺,分析了粒子预热温度、浇注温度和充型压力工艺因素对金属液充型过程的影响。
补充资料：负压铸造
采用负压造型法生产铸件的一种铸造方法。负压造型又称真空密封造型。这一方法使用的砂箱装有能通气的滤网或蛇形管，通过抽气管与真空泵相连接；使用的造型材料为不含水分和粘结剂的干砂。造型时，先在模板上覆盖一层塑料薄膜，用真空泵抽气，使薄膜紧贴在模板上，然后套上砂箱，再往砂箱中充填造型材料，经震实刮平之后，用塑料薄膜覆盖砂箱顶面，接通真空泵吸出砂粒间的空气，使砂型内形成负压，同时撤除模板真空，让塑料薄膜转而吸附在铸型内腔面上，砂型靠压力差的作用具有一定的强度和硬度。经起模、合箱、浇注、凝固冷却后撤除负压，即可得到所需铸件。负压铸造能应用于各种合金的铸造，是20世纪70年代出现的一种新方法。用这种方法制造出的铸件轮廓清晰，表面光洁，尺寸精确，既适于浇注厚壁铸件，更适于浇注薄壁铸件，有些小直径的孔眼，也能直接铸出。由于造型材料中不含水分和粘结剂，铸件不易产生气孔等缺陷，内在质量较好，砂处理简化，铸件落砂方便，但操作较复杂，生产率低。