1) lower degree of polymerization
较低聚合度
2) low polymerization degree
低聚合度
1.
The development of PVC resin with low polymerization degree;
低聚合度PVC树脂的开发研究
2.
Poly(vinyl acetate) with low polymerization degree had been prepared through radical polymerization using AIBN as initiator in methol solution.
以甲醇为溶剂,偶氮二异丁腈(AIBN)为引发剂,采用自由基聚合方法合成了低聚合度聚醋酸乙烯酯,并对其结构进行了表征。
3.
Poly(vinyl chloride) (PVC) resin with low polymerization degree ,high porosity and less skin exhibits: low aggregation degree of primary particles, easy diffusion for micromolecule and easy processing.
疏松少皮低聚合度聚氯乙烯(PVC)树脂具有初级粒子小、聚集程度低,小分子易扩散和易塑化加工等特点,在制备氯化聚氯乙烯(CPVC)树脂等方面具有良好的应用。
3) PVC resin with low degree of polymerization
低聚合度PVC
1.
The development of PVC resin with low degree of polymerization;
低聚合度PVC树脂的研制
4) ultra low polymerization degree
超低聚合度
1.
The formula optimization of PVC with ultra low polymerization degree;
超低聚合度PVC配方的优化
5) lower basicity
较低碱度
1.
A study on improving intensity of lower basicity sinter;
改善较低碱度烧结矿质量的研究
6) low polymer loading
低聚合物浓度
补充资料：低聚合度聚氯乙烯
分子式：
CAS号：
性质：指平均聚合度600以下的聚氯乙烯树脂。工业产品300～400间。孔隙率高具有较好的吸油能力，树脂熔融温度低，加工流动性好，塑化时间短。以氯乙烯在较高温度下(60～80℃)或在链转移剂存在下，用悬浮法聚合而得。可用挤出压延法生产硬片和硬板、透明瓶、各种注塑制品，可替代部分糊用树脂和掺混树脂用于配制PVC糊。还用作固体粉末涂料，高聚合度树脂的加工助剂。
CAS号：
性质：指平均聚合度600以下的聚氯乙烯树脂。工业产品300～400间。孔隙率高具有较好的吸油能力，树脂熔融温度低，加工流动性好，塑化时间短。以氯乙烯在较高温度下(60～80℃)或在链转移剂存在下，用悬浮法聚合而得。可用挤出压延法生产硬片和硬板、透明瓶、各种注塑制品，可替代部分糊用树脂和掺混树脂用于配制PVC糊。还用作固体粉末涂料，高聚合度树脂的加工助剂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。