1) solid-solid state synthesis method at room temperature
室温固-固相化学反应法
2) solid-solid state synthesis method
室温固-固化学反应法
3) room temperature solid-state reaction
室温固相化学反应
1.
Surface-modified lead iodide nanorods were synthesized by one-step room temperature solid-state reaction of lead nitrate with potassium iodide in the presence of a nonionic surfactant, polyethyl- ene glycol.
以硝酸铅和碘化钾为原料,在体系中添加表面活性剂聚乙二醇(PEG),采用一步室温固相化学反应制备出聚乙二醇表面修饰的碘化铅纳米棒,利用X射线衍射,红外光谱,透射电子显微镜,扫描电子显微镜,热分析和元素分析等手段对其进行了表征。
4) the ball-grinding solid state reaction
室温球磨固相化学反应
1.
The host of fluorescence powder BaMgAl10O17:Eu2+ was prepared by the ball-grinding solid state reaction at room temperature.
采用室温球磨固相化学反应法制备蓝色荧光粉BaMgAl10O17:Eu2+的基质材料,借鉴表面扩散原理对蓝粉进行铕元素的掺杂,用活性碳粉还原得到BaMgAl10O17:Eu2+。
5) solid-state chemical reaction method
固相化学反应法
1.
Precursor of nano-sized Cu-Mn composite oxide was synthesized by solid-state chemical reaction method with cupric acetate\,manganese acetate\ and oxalic acid\ as the raw materials.
以乙酸铜、乙酸锰与草酸为原料,采用固相化学反应法制备了纳米铜锰复合氧化物前驱物,利用均匀设计考察了微波功率与加热时间、热分解温度及时间对产物粒径的影响。
6) solid state reaction at room temperature
室温固相反应
1.
MnO 2 was prepared with solid state reaction at room temperature, MnO 2 powder prepared with this method was nanosized and had large surface area(300m 2/g).
由室温固相反应制备 Mn O2 。
补充资料：化学反应方程式配平法
（一）最小公倍数法
这种方法适合常见的难度不大的化学方程式。例如，kclo3→kcl+o2↑在这个反应式中右边氧原子个数为2，左边是3，则最小公倍数为6，因此kclo3前系数应配2，o2前配3，式子变为：2kclo3→kcl+3o2↑，由于左边钾原子和氯原子数变为2个，则kcl前应配系数2，短线改为等号，标明条件即：
2kclo32kcl+3o2↑
（二）奇偶配平法
这种方法适用于化学方程式两边某一元素多次出现，并且两边的该元素原子总数有一奇一偶，例如：c2h2+o2──co2+h2o，此方程式配平从先出现次数最多的氧原子配起。o2内有2个氧原子，无论化学式前系数为几，氧原子总数应为偶数。故右边h2o的系数应配2（若推出其它的分子系数出现分数则可配4），由此推知c2h2前2，式子变为：2c2h2+o2==co2+2h2o，由此可知co2前系数应为4，最后配单质o2为5，写明条件即可：
2c2h2+5o24co2+2h2o
（三）观察法配平
有时方程式中会出现一种化学式比较复杂的物质，我们可通过这个复杂的分子去推其他化学式的系数，例如：fe+h2o──fe3o4+h2，fe3o4化学式较复杂，显然，fe3o4中fe来源于单质fe，o来自于h2o，则fe前配3，h2o前配4，则式子为：3fe+4h2o＝fe3o4+h2↑由此推出h2系数为4，写明条件，短线改为等号即可：
3fe+4h2ofe3o4+4h2↑
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条