1) isobaric thermal gradient CVI
等压热梯度CVI
2) thermal gradient CVI
热梯度CVI
1.
Microstructure and properties of C/C composites prepared by thermal gradient CVI process;
热梯度CVI C/C材料的结构与性能
2.
Using nitrogen, hydrogen respectively as the carrier gas, the C/C composite was fabricated by the thermal gradient CVI process under the condition of 1000℃,0.
在1000℃,0 5kPa丙烯分压条件下,以N2、H2为载气和无载气情况下于热梯度CVI炉中制备了C/C复合材料,研究了载气特别是氢气对材料基体热解炭显微结构的影响。
3.
The carbon cloth and carbon fiber felt are laminated alternately and then needled to prepare the porous carbon/carbon preforms, from which the carbon/carbon composites for aircraft brakes are fabricated by the thermal gradient CVI process.
以炭布与炭纤维薄毡交替成叠层 ,采用针刺技术在垂直布面方向引入增强纤维 ,制成准三维预制体 ,在自行研制的热梯度CVI炉中制备了航空刹车用C/C复合材料 ;采用偏光显微镜研究了沉积炭的显微结构 。
3) Constant pressure gradient
等压力梯度
4) isallobaric gradient
等变压梯度
5) imparity pressure gradient
压力梯度不等
6) positive pressure CVI
正压CVI
1.
The reaction gases can be effectively utilized in the positive pressure CVI process.
研究表明 ,当沉积温度低于 90 0℃时 ,可以避免或减少沉积过程中炭黑的生成 ,在该前提下 ,正压CVI工艺可在较短时间内制备出具有合理微观组织结构的C/C复合材料制件 ,因此提高了反应气体的利用率 ,正压CVI工艺是一种低成本的C/C复合材料制备工
补充资料：等压反应热
分子式：
CAS号：
性质：在等压过程中化学反应放出或吸收的热(始态和终态的温度与热源相同)。。等压反应热(Qp)也称反应焓(reaction enthalpy)。上式是在系统只做体积功时才成立(H为焓)。
CAS号：
性质：在等压过程中化学反应放出或吸收的热(始态和终态的温度与热源相同)。。等压反应热(Qp)也称反应焓(reaction enthalpy)。上式是在系统只做体积功时才成立(H为焓)。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条