1) Vanadium Corbides
钒碳化物
2) vanadium carbonitfidc
钒碳氮化物
3) Vanadium oxide-carbon positive electrode
钒氧化物-碳电极
4) V-rich MC
MC型富钒碳化物
5) vanadium carbonitride
碳氮化钒
1.
The effect of technical parameters on nitrogen content in vanadium carbonitride is investigated.
研究了一步法合成碳氮化钒的生产工艺及工艺参数对碳氮化钒氮含量的影响。
6) vanadium carbide
碳化钒
1.
Superfine microstructure analyses of vanadium carbide in high vanadium high speed steel;
高钒高速钢中碳化钒的微细结构分析
2.
The vanadium carbide/high chrome cast iron composite layer was formed on the surface of low-cost ZG310-570 by combining LFC process and casting penetration process.
结合消失模铸造工艺和铸渗表面强化技术,在廉价的ZG310-570表面形成一层碳化钒/高铬铸铁复合层。
3.
The process involved the preparation of vanadium carbide which can be prepared from V 2O 3 by vacuum carbon reduction and then being nitrified to vanadium nitride by nitrogen gas.
以V2 O3为原料 ,采用真空还原方法制备出碳化钒 ,生成的碳化钒直接进行渗氮制备出碳氮化钒。
补充资料：碳化钒
分子式：
CAS号：
性质：银白色晶体。密度5.25～5.4g/cm3。熔点2750℃。比石英略硬。可由五氧化二钒用焦炭还原制得。主要用于制造钒钢。
CAS号：
性质：银白色晶体。密度5.25～5.4g/cm3。熔点2750℃。比石英略硬。可由五氧化二钒用焦炭还原制得。主要用于制造钒钢。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。