1) filling speed measurement
充型速度测试
2) Filling Velocity
充型速度
1.
The Influence of Various Process Parameters on the Liquid Metal Filling Velocity in Gray Iron Casting Produced by EPC V Process;
铸铁件EPC-V法工艺因素对充型速度的影响
2.
The result indicats that there are few blowholes,inclusions except misrun in the casting with the filling velocity of 25mm/s,and the casting was formed with some blowholes、inclusions with the filling velocity of 40mm/s,while the casting was form.
研究了薄壁铝合金铸件真空吸铸充型速度对其内部质量的影响,对一种200mm×180mm,壁厚为2。
3.
The metal filling velocity increases with the reduction of pattern density and coating thickness, and the increase of pouring temperature.
研究了模样密度、涂层厚度、浇注温度、真空度等工艺参数对可控气压下镁合金消失模铸造时液态金属的充填形态和充型速度的影响,以及充型速度与充型形态之间的关系。
3) filling speed
充型速度
1.
The filling speed of lost foam cast iron casting was measured by use of an integrated set of experimental equipment and a specially designed computer acquisition system.
研究了负压度、模样密度、浇注温度、金属静压头等工艺因素对消失模铸铁件充型速度的影响规律。
4) mold filling velocity
充型速度
1.
Study on mold filling velocity in AZ91 magnesium alloy LFC process with vacuum;
AZ91镁合金负压消失模铸造充型速度的研究
2.
The influence of processing parameters on the mold filling velocity during investiment casting was investigated by using an integrated system of experimental equipment and a specially designed computer data acquisition device.
用消失模铸造试验装置和计算机数据采集系统研究了工艺因素对充型速度影响的规律。
3.
The mold filling velocity of AI alloy melt in lost foam casting process was investigated by X-ray technology and other method.
充型中期,充型速度增加较快;而充型末期,由于温度降低以及气压升高,充型速度锐减。
6) testing speed
测试速度
1.
The results of computer simulation show that this method does not require the sampling interval to satisfy the Nyquist sampling criteria and only needs few sampling points to attain very high testing precision,so we can improve the testing speed and effectively reduce the truncation error caused by finite scanning plane on the premise of ensuring t.
计算机模拟结果表明 ,这种方法不要求取样间隔一定要满足奈奎斯特取样准则 ,只需较少的取样点数即可达到很高的测试精度 ,从而能够在保证测试精度的前提下 ,提高测试速度并有效减小由于有限扫描面所引起的截断误差 。
2.
The malfunction of UST-4 evenness tester was reduced by optimizing the temperature, the humidity, testing speed and other measures.
介绍了UST-4型条干均匀度仪工作原理,通过优化温湿度、测试速度等措施,降低了该仪器分析样品的故障率,同时对常见仪器故障的影响因素进行了分析,确保该仪器稳定运行。
补充资料：测试结果可接受性的检查和最终测试结果的确定
测试结果可接受性的检查和最终测试结果的确定
check of the acceptability of test results and determination of the final test result
C凡(3)二3.3d，时，取此3个结果的平均值作为最终侧试结果;否则取它们的中位数作为最终测试结果。。，为重复性标准差(即在重复性条件下所得侧试结果的标准差)。 在口田T 11792一1989中还对重复性和再现性条件下所得侧试结果可接受性的检查方法和最终测试结果的确定做了详细讨论和规定。(马毅林)ceshi 11叩uo kejieshCxjxing d6 iiancha he zuizhong ceshi】i闪旧de que心ing测试结果可接受性的检查和最终测试结果的确定(checkof山eac，ptability of test，ults助ddsterminationofthefi耐testresult)在商品检验中进行一次测试的情形不多见，当得到一个测试结果时，所得结果不可能直接与给定的重复性标准差作可接受性的检查。对测试结果的准确性有任何疑问时都应再进行一次测试。所以，对两个测试结果进行可接受性的检查是一般的情况。 可接受性的检查，实际上是一种统计检验。任何两个测试结果只要能通过可接受性的统计检验即可认为是一致的，均可接受。比如，在重复性条件下，所得结果之差的绝对值(下称绝对差)不超过相应的重复性限r(见重复性和再现性)的值，则认为两个结果是一致的，均可接受;如果两个侧试结果的绝对差超过r，则认为它们是不一致的，必须增加测试。 按国家标准《测试方法的精密度在重复性或再现性条件下所得测试结果可接受性的检查和最终测试结果的确定》(GBIT 1 1792一1989)，在重复性条件下，如果两个测试结果的绝对差不超过r的值，可取两个侧试结果的平均值作为最终测试结果。如果两个结果的绝对差超过r的值，并且测试费用较低，须再做两次测试。当4个结果的极差(即其中的最大值与最小值之差)不超过相应的临界极差c，瓜(4)二3.6a，时，取4个结果的平均值作为最终测试结果。如果两个结果的绝对差超过r的值，并且测试费用较高时，只须再作一次测试。当3个结果的极差不超过相应的临界极差