1) MB-adsorption value
MB吸附值
2) methylene blue value
MB值
1.
Study on effect of methylene blue value of manufactured sand on performance of concrete
研究了机制砂亚甲蓝(MB)值与石粉、粘土含量及粘土特性的关系,试验分析了机制砂MB值在0。
3) iodine adsorption value
碘吸附值
1.
The iodine adsorption values of rayon-based activated carbon fibers under different activation conditions are comprehensively studied.
介绍了活性炭纤维与活性炭相比较更加优良的性能和更加广泛的用途,叙述了活性炭纤维生产的3种主要工艺,叙述了当前中国活性炭纤维的生产现状,研究了不同活化条件下黏胶基活性炭纤维的碘吸附值。
2.
The methyllene cyanine adsorption value and the iodine adsorption value of the product were tested.
本文以稻壳为原料制备粉末活性炭,对其进行了亚甲基蓝吸附值和碘吸附值的测试。
3.
Comparison and analysis were made for existence several activated carbon iodine adsorption value measurement methods based on the measurement result.
对现有的几种活性炭碘吸附值的测试方法进行了比较和分析,分别用这些方法测定了一些活性炭的碘吸附值,讨论了这些方法的优缺点,针对GB/T7702。
4) adsorption value
吸附值
1.
Taking bamboo leftover as the raw material, adventitious granulated charcoal is extracted by cross test, which is good in strength with high iodine adsorption value.
以竹下脚料为原料,通过正交试验法制取不定形颗粒炭,经检测其强度好,碘吸附值高,优于LY/T1125-1993《提取黄金用颗粒活性炭》标准A类(椰壳原料)指标,可作为椰壳活性炭的替代品用于黄金吸附,为黄金生产提供了新的活性炭品种。
2.
The iodine adsorption value and methylene blue adsorption value are 1520.
研究结果表明,活化剂与稻壳的质量比为3∶1,在800℃活化1h,制得的活性炭碘吸附值为1520。
5) iodine number
碘吸附值
1.
The author analyses the affect on activated carbon iodine number of the craft condition, handling process and test environment, and looks for the best of the craft condition and the test environment in order to acquire activated carbon of the high iodine number.
分析活性炭生产过程中的工艺条件、后处理过程和测试环境对活性炭碘吸附值高低的影响,寻找活性炭生产的最佳工艺条件和测试环境,以获得高碘吸附值的活性炭。
2.
The relationship between the Iodine number,Methylene blue adsorption,Caramel adsorption and the pore structure of activated carbon have been analyzed.
分析测定了原料及活化方法不同的几种活性炭的常规性质和孔隙性质，研究了活性炭的碘吸附值、亚甲基蓝脱色力及焦糖脱色力与活性炭孔隙结构之间的关系，得知活性炭对这３种物质的吸附能力，取决于其孔隙结构中半径０。
6) oil adsorption
油吸附值
补充资料：特性吸附与半胶束吸附
特性吸附与半胶束吸附
specifical adsorption and hemi-micelle adsorption
texing xifu yu banJ旧oshu xifu特性吸附与半胶束吸附(speeifieal adsorp-tion and hemi一mieelle adsorption)矿物一水界面的吸附的两种形式。特性吸附是因矿物表面与溶液中某种组分(离子或分子)有特殊的亲和力而产生的吸附，也称特殊吸附。特性吸附不仅可以改变电位的数量而且还可以改变电位的符号。例如，刚玉(A12O3)在NaZSO‘或RSO;Na(烷基硫酸钠)溶液中，电动电位随溶液浓度的增大由正值逐渐减小，直至变为负值，说明刚玉对50矛一或RSO不离子有特殊的吸引力。半胶束吸附是水溶液中的表面活性剂在矿物表面产生的吸附，当吸附量达到一定值以后，由于烃基的缔合作用，表面活性剂的离子或分子在矿物表面上形成紧密的吸附层，这类似于溶液中形成的胶束结构，但所形成的“胶束”与溶液中形成的胶束不同，只有二维空间，故称这类吸附为半胶束吸附。矿物表面对胺类捕收剂的吸附，当胺的浓度较大时，常可以产生半胶束吸附。 (龚焕高)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条