1) copper/steel composite materials
铜/钢复合材料
2) copper-steel back composite
铜-钢背复合材料
3) copper-steel clad material
铜钢复合材料
1.
The process techniques,properties and connection of copper-steel clad material are introduced,the economic properties of galvanized steel,copper-steel clad material and copper are discussed,application of copper-steel clad material in ground grid of transformer substation are prospected.
论述了铜钢复合新材料的生产工艺、性能及连接方式,并对接地用材料热镀锌钢、铜钢复合材料及铜进行了经济性分析,阐述了铜钢复合材料在变电站接地网的应用前景。
4) copper-stainless steel composites
铜-不锈钢复合材料
1.
By means of synergistic accelerated corrosion test and electrochemical measuring,the corrosion behavior of copper-stainless steel composites and Cu in HSO_(3)~(-)/Cl~- media was studied.
采用选择腐蚀技术,提取了铜-不锈钢复合材料中的纤维相,并测定了纤维相电极电位。
5) steel-base copper-plastic compound material
钢基铜塑复合材料
补充资料：钯/铜复合材料
分子式：
CAS号：
性质：由钯和铜形成的复合材料。不形成连续固溶体，亦无有序无序转变，导电率比传统的钯铜合金大大提高，随铜含量增加而呈直线上升，其值接近理论计算值。Pd/Cu18, Pd/Cu42,Pd/Cu60,Pd/Cu72的导电率分别为19.3m/Ω·mm2，31.4m/Ω·mm2，40.16m/Ω·mm2和45.6m/Ω·mm2。Pd/Cu42的理论值33.2m/Ω·mm2；Pd/Cu40合金的电导率仅为3m/Ω·mm2。Pd/Cu复合材料的硬度、屈服极限、抗拉强度和伸长率几乎与成分无关。它们的维氏硬度为882.6MPa。采用纤维复合方法制取。在铜管中装入5000根钯丝，经大变形量冷加工和中间退火而制成40.5-2mm的丝材。也可用钯片和铜片叠合卷紧挤压拉伸以及混合粉料用加热等静压方法。作汽车闪光灯继电器接点。
CAS号：
性质：由钯和铜形成的复合材料。不形成连续固溶体，亦无有序无序转变，导电率比传统的钯铜合金大大提高，随铜含量增加而呈直线上升，其值接近理论计算值。Pd/Cu18, Pd/Cu42,Pd/Cu60,Pd/Cu72的导电率分别为19.3m/Ω·mm2，31.4m/Ω·mm2，40.16m/Ω·mm2和45.6m/Ω·mm2。Pd/Cu42的理论值33.2m/Ω·mm2；Pd/Cu40合金的电导率仅为3m/Ω·mm2。Pd/Cu复合材料的硬度、屈服极限、抗拉强度和伸长率几乎与成分无关。它们的维氏硬度为882.6MPa。采用纤维复合方法制取。在铜管中装入5000根钯丝，经大变形量冷加工和中间退火而制成40.5-2mm的丝材。也可用钯片和铜片叠合卷紧挤压拉伸以及混合粉料用加热等静压方法。作汽车闪光灯继电器接点。