1) Ti-Cu based alloys
Ti-Cu合金
2) Cu-Ti alloy
Cu-Ti合金
1.
The effect of Zr on heat-resistance of Cu-Ti alloy was investigated.
研究了Zr的加入对Cu-Ti合金耐热性能的影响。
2.
The layer of Cu-Ti alloy was prepared by arc ion plating(AIP) on the copper substrate.
采用同基合金电弧离子镀方法,在紫铜基体上制备了Cu-Ti合金薄膜,研究了弧电流和靶-基距离对膜层质量、沉积速率的影响。
3) Ti-Ni-Cu Alloy
Ti-Ni-Cu合金
1.
Effect of long-term annealing on the martensitic transformation behavior of Ti-Ni-Cu alloy ribbons
长时间热退火对Ti-Ni-Cu合金条带马氏体相变行为的影响
2.
The results indicate that TME of Ti-Ni-Cu alloy only exists in the heating process,and TME occurs both in B19′→B2 and B19→B2 transformation during heating process.
结果表明:温度记忆效应仅在Ti-Ni-Cu合金的逆转变加热过程出现,在单斜结构马氏体与母相逆相变(B19′→B2)及正交结构马氏体与母相逆相变(B19→B2)过程中均能发生温度记忆效应;在随后的完全循环过程中,温度记忆记忆效应不再出现,DSC相变曲线又“恢复”到其原始形态;而在马氏体相变冷却过程中未发现温度记忆效应。
4) Cu-Cr-Ti alloy
Cu-Cr-Ti合金
1.
The microstructures of Cu-Cr-Ti alloy were obtained by alloying way at different cooling conditions.
采用加钛合金化的方法得到了不同冷却条件下Cu-Cr-Ti合金的凝固组织。
5) Cu-Ti-Zr alloys
Cu-Ti-Zr合金
6) Ag-Cu-Ti alloy
Ag-Cu-Ti合金
1.
45%C using Ag-Cu-Ti alloy reinforced by TiN particles as composite filler were carried out with heating temperature of 920 ℃ and dwell time of 5 min.
向Ag-Cu-Ti合金中加入TiN颗粒组成复合钎料。
补充资料：A1-Cu-Co合金中十次对称准晶单晶体及其衍射图
A1-Cu-Co合金中十次对称准晶单晶体及其衍射图
‘ Al Cu—Co合金中十次对称准晶堕晶体e1)及其衍射圈(z) 中国科学盹垒禹研览听供稿