2) sodium aluminate crystallization
铝酸钠结晶
3) crystalline aluminum chloride
结晶氯化铝
1.
Experimental study was conducted on the preparation of crystalline aluminum chloride from industrial diluted hydrochloric acid and calcium aluminates under atmospheric pressure condition.
通过对常压下采用工业稀盐酸和铝酸钙制备结晶氯化铝净水剂的试验研究,考察了铝酸钙低浓度盐酸浸取时原料配比、浸出时间、浸出温度对三氧化二铝溶出率的影响,并对三氯化铝结晶阶段的机理进行了探讨,实验结果表明低浓度工业废酸可以用于制备结晶氯化铝。
4) crystalline aluminosilicate
结晶硅酸铝
5) crystalline alumolite
结晶水铝石
6) crystal aluminum sulphate
结晶硫酸铝
1.
Methylaluminoxane(MAO) was prepared by adding solid powder of crystal aluminum sulphate to trimethylaluminum(TMA) toluene solution under the conditions of reaction temperature 40℃,reaction time 30h,rate of material inputting 5g/min,and TMA concentration 3.
采用将结晶硫酸铝固体粉末缓慢加入到三甲基铝(TMA)甲苯溶液中的间接水合成工艺,在反应温度为40℃,反应时间为30 h,加料速度为5 g/min,硫酸铝结晶水为12,TMA摩尔浓度为3。
补充资料：定向结晶铝镍钴合金磁体
定向结晶铝镍钴合金磁体
alnic'o magnet with directed grain
d一ngx一angleJ一ng IUn一egu hejlne一tl定向结晶铝镍钻合金磁体(alnieo magnetwith direeted grain)用铝镍钻系合金铸造的具有晶粒择优取向的高性能磁体。铸造铝镍钻磁体的磁结构受其晶体结构的影响。晶体的<1。①为易磁化方向，发展完善的(100>晶体织构(柱状晶)可使磁体获得更好的磁性能。 在商业磁体中，根据定向结晶的完善程度可分为部分晶体取向磁体和完全晶体取向磁体。高剩磁和高矫顽力型铝镍钻合金均可制成定向结晶磁体。由典型的高剩磁合金制成的定向结晶磁体(美国牌号AlnicosDG，中国牌号LNG52)的最大磁能积(BH)。二由等轴晶的32~40kJ/m3提高到柱状晶的52一56 kJ/m3;由典型的高矫顽力型合金制成的定向结晶磁体(Alnicog型，LNGT72)的(BH)、，由等轴晶的25一4okJ/m3提高到柱状晶的65~sokJ/m3。部分晶体取向磁体的磁性能介于等轴晶磁体和完全晶体取向磁体的性能之间。用合金制造定向结晶磁体的工艺与普通铸造磁体工艺的主要差别在于，前者采用一种特殊的铸造工艺。该工艺的特点是，将融熔的合金浇注到定向导热的铸模中，这种铸模设计成周围绝热、端部导热的结构，以确保晶粒沿导热方向生长。此外应当注意的是，当这种柱状晶磁体在磁场热处理、磁化时以及在磁路结构的应用中，均须沿柱状晶长大的方向进行。定向结晶磁体的应用与普通铝镍钻磁体的应用相同(见铭镍钻系永磁合金)，只是由于性能提高，使得所用磁体的体积和重量相应减小。 (肖文涛)