1) initial solidification
初始凝固
1.
Recent development of heat transfer during initial solidification in continuous casting;
连铸初始凝固区域传热研究进展
2.
Influence of mould cooling intensity on the strand shell homogeneity in the initial solidification areas;
结晶器冷却强度对铸坯初始凝固均匀性的影响
3.
Experimental measurements and numerical analysis have been conducted to clarify the high frequency magnetic field distribution in the region of initial solidification within the soft contact EMCC (electromagnetic continuous casting) mold of billet.
分析结果表明：采用通体切缝形式的结晶器具有比封闭切缝形式结晶器更好的透磁性；增加感应线圈匝数时，可增大高频磁场在铸坯初始凝固区的有效作用范围：当液态金属弯月面位于感应线圈上沿附近时，高频磁场作用于初始凝固区的有效作用范围较大、电磁压力分布的不均匀程度较小，有助于获得高表面质量的铸坯。
2) initial solidification temperature
初始凝固温度
1.
The influence of initial solidification temperature on the microstructure at the brazed joint zone was investigated.
研究了钎焊温度对钎焊接头微观组织的影响 ,并利用图像软件Image ProPlus确定了不同初始凝固温度下α (Al)相在钎焊接头中的体积分数。
3) initial condensing
初始凝结
4) initial anticoagulation
初始抗凝
5) primary consolidation
初始固结
6) initial solidification
初期凝固
1.
The initial solidification phenomena of low carbon steel,which solidifies with a hypoperitectic reaction in the continuous casting,have been modeled.
为了模拟连铸过程中具有亚包晶反应的低碳钢的初期凝固现象,利用浸渍实验,测量了铸坯的二次树枝晶间距;利用有限元的一维传热汁算,求得冷却速度与二次树枝晶间距的关系式;探讨了传热阻力等参数对铸坯的冷却速度、凝固不均一度的影响。
2.
The temperature fields and stress fields of initial solidification shell in the mould of smooth and groove were calculated,the difference between the tWo condition was analyzed and effect to dritial solidiflcation process caused by model of grooves was stUdied .
以初期凝固坯壳为研究对象，在结晶器内壁纵向划分沟槽，建立数学模型，计算划分沟槽与不划分沟槽结晶器内铸坯的温度场和应力场，研究沟槽内壁结晶器对铸坯初期凝固过程的影响。
补充资料：初始
初始（或写作始初，8年十一月）是西汉时期孺子婴的第2个年号，也是他的最后一个年号，共计1个月。初始元年十二月王莽即位，建立新朝，以初始元年十二月朔癸酉为正月之朔，改元始建国，西汉灭亡。
《资治通鉴》写作“始初”，《汉书·王莽传》作“初始”。居延汉简则也是“初始”，另外有出土记为初始元年的文物。
中央研究院之两千年中西历转换将初始元年十一月作西元8年12月17日。初始年号终结于9年1月14日。
《资治通鉴》写作“始初”，《汉书·王莽传》作“初始”。居延汉简则也是“初始”，另外有出土记为初始元年的文物。
中央研究院之两千年中西历转换将初始元年十一月作西元8年12月17日。初始年号终结于9年1月14日。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条