1) Al-Mn alloy
铝-锰合金
1.
Molten salt electroplating processing of Al-Mn alloys and properties of coating had been investigated in this paper.
对熔盐电镀铝锰合金的电镀工艺、镀层性能进行了研究,结果表明:所获得的铝-锰合金镀层平滑致密,光亮,附着力良好,耐蚀性优良,当锰含量超过30%时,镀层转化为非晶态结构。
2) Al-Mn allays
锰铝合金
1.
The solid-liquid mixed casting of Al-Mn allays was studied by adding same alloys powder, the structure and performance of the material prepared by solid-liquid mixed casting was analyzed.
2%;优于传统铸造和半固态铸造合金,使难以应用的高锰铝合金有了应用可能。
3) aluminum manganese alloy
铝锰合金
1.
In this paper, a spectrophotometry for determination of manganese in high resistance aluminum manganese alloy is reported.
介绍了一种用分光光度法测定铝锰合金中锰含量的测定方法。
4) 3003 aluminium-manganese alloys
3003铝锰合金
1.
The microstructure and mechanical properties of as-cast and homogenized 3003 aluminium-manganese alloys grain-refined by Ti addition using different methods were investigated by SEM and EDS.
用SEM和EDS等方法研究了细晶铝锭熔铸的3003铝锰合金以及Al-10Ti中间合金、Al-5Ti-1B中间合金细化的3003铝锰合金铸态及均匀化处理状态的组织和力学性能。
5) ferroaluminium-manganese
铝锰铁合金
1.
Deoxidising high quality aluminium killed steel with silicon-free ferroaluminium-manganese instead of purd aluminium exists some problems such as the production cost is increased,steel quality is impaired etc.
高品质的铝镇静钢以无硅铝锰铁合金代替纯铝脱氧应用后存在成本增加和影响钢质量等问题。
6) aluminium-manganese-magnesium alloy
铝锰镁合金
1.
After samples were dissolved by acid,quantitative barium chloride and superfluous sodium hydroxide were used to totally precipitate and separate the disturbing elements in aluminium-manganese-magnesium alloy such as manganese,iron and magnesium,which separated manganese first with sextic methyl tetramine and then separated magnesium and iron secondly.
试样以酸溶解后,采用定量的氯化钡与过量的氢氧化钠一次性沉淀分离铝锰镁合金中的锰、铁、镁干扰元素,再用氢氧化钠沉淀分离铁、镁的二次沉淀与铝分离。
补充资料：电解法生产铝锰合金
电解法生产铝锰合金
production of aluminium-manganese alloy by electrolysis
d ianJ一efo shengehan IUmeng hej!n电解法生产铝锰合金(produetion of alu-minium一manganese alloy by eleetrolysis)在铝电解槽中电解冰晶石一氧化铝一氧化锰熔体制取铝锰合金的过程。属铝锰合金生产新工艺，为熔盐电解法生产铝墓母合金的一种方法。 仁业h应用的铝锰合金一般含锰在2%以下{铝锰呼合金含锰10%左一右。铝锰合金的焊接性能好，强度和耐腐蚀性也比L业纯铝好，可塑性较好，可轧制成板、棒、带、线和箔多种型材，广泛应用于各工业部门。 对掺法生产铝锰合金是传统的方法，包括制备铝锰毋介金、熔化一冷业纯铝、加母合金、均质和净化、除涟、铸锭等过程。与对掺法相比，电解法生产铝锰合金具有的L艺简单、合金成分均匀、生产成本低等优点，电解法生产铝锰合金的技术条件，包括生产过程所采咐的f艺参数、加料制度和铝锰合金的锰含量。 l_艺叁数是指电解过程中所控制的技术数据。在臼k八电解槽进行电解时，电解槽的工作电压采用4.3一d.生V，冰八{;石比为26一2.8，电解温度控制在1233K了。仃 加料制度是指向铝电解槽中添加氧化锰的方法。电解法生产铝锰合金用的含锰原料是二氧化锰，一般含锰48%二氧化锰添加到电解质壳面上，待铝电解栖打壳加卜时进入电解质中。每2一3h添加次，添加的数量根据合金中的锰含量计取。二氧化锰中锰的回收率为9。%。 铝锰合金的锰含量是电解法生产铝锰合金需要控制的技术条件之一这种方法适宜生产含锰量在2%以F的低铝锰介金，因为当合金中的锰含量超过5%伟贪，铝电解槽便不能正常工作。 (赵恒先徐树田)