1) intumescent coatings
膨胀型涂料
2) intumescent fire-retardant coatings
膨胀型防火涂料
1.
This paper narrates raw material selection, technology design and compositions optimization of silicone/acrylic latex intumescent fire-retardant coatings; and discusses physical and chemical performances and technical index.
叙述了硅丙乳液膨胀型防火涂料研制过程中的材料选择、工艺设计及配方优化,对该涂料的理化性能、技术指标等进行了全面讨论。
3) intumescent paints
膨胀型阻燃涂料
1.
A intumescent paints with good adhesion for PP board was prepared by proper choice of resins,solvents, additives and flame retardants etc.
通过表面处理和选择合适的树脂、溶剂、助剂、膨胀型阻燃剂等,制备出用于PP板表面的膨胀型阻燃涂料。
4) intumescent flame-retardant coating
膨胀型防火涂料
1.
Mechanism and development of intumescent flame-retardant coatings;
膨胀型防火涂料的阻燃机理及其研究进展
2.
An intumescent flame-retardant coating was prepared using the determinated unsaturated polyester resin and epoxy resin as matrix resins,ammonium polyphosphate,melamine and pentaerythritol as flame-retardant assistants,by adding fillers and other assistants.
以不饱和聚酯和环氧树脂双组分作为基体树脂,以聚磷酸铵、三聚氰胺和季戊四醇为防火助剂,辅以填料和其他助剂,配制膨胀型防火涂料。
3.
An intumescent flame-retardant coating was prepared using unsaturated polyester resin and epoxy resin as two-component matrix resins, common flame-retardant system—ammonium polyphosphate, melamine and pentaerythritol as flame-retardant assistants, expandable graphit.
本论文对防火涂料的树脂基体、阻燃体系、颜填料组分的种类和用量进行了筛选,通过一系列的正交实验和横向比较实验完成了防火涂料配方的优化,确定出了以不饱和聚酯树脂和环氧树脂拼用作为双组分树脂基体,以脱水成炭催化剂(聚磷酸铵JLS-APP)、成炭剂(季戊四醇PER)和发泡剂(三聚氰胺Mel)即传统的P-C-N体系作为本实验的阻燃体系,以可膨胀石墨为膨胀体系的协同增效剂,添加填料TiO_2,辅以溶剂和其他助剂,配制膨胀型防火涂料。
5) intumescent coating
膨胀型防火涂料
1.
More and more attention has been focusing towards intumescent coating because it has high thermal insulation against flame and good decorative property.
膨胀型防火涂料具有涂层薄、装饰效果好，遇到火焰或高温作用时涂层膨胀发泡，防火隔热效果较好等特点，国内外都正在开展广泛研究和推广使用。
6) intumescent steel structure fire-retardant coating
膨胀型钢结构防火涂料
1.
The effects of charring agents′ type as well as the ratios of compound charring agents on the fire-protective properties of the intumescent steel structure fire-retardant coatings (ISSFRC) were investigated.
研究了成炭剂种类及其复配技术对超薄膨胀型钢结构防火涂料性能的影响。
补充资料：膨胀型防火涂料
分子式：
CAS号：
性质：通过形成泡沫炭化层以阻挡外部热源的一类防火涂料。成膜后，常温下是普通的漆膜。在火焰或高温下，涂层发生膨胀炭化，形成一个比原来膜厚度大几十倍甚至上百倍的不易燃的海绵状炭质层，使外界火源与基材隔绝，从而起到阻燃作用。通常以基料、发泡料、成炭剂、脱水成炭催化剂、防火添加剂、无机颜填料、辅助剂等制成。这类漆遇小火不燃，离火自熄，具有防延燃性。广泛应用于建筑、车辆、仓库、电器、包装等。
CAS号：
性质：通过形成泡沫炭化层以阻挡外部热源的一类防火涂料。成膜后，常温下是普通的漆膜。在火焰或高温下，涂层发生膨胀炭化，形成一个比原来膜厚度大几十倍甚至上百倍的不易燃的海绵状炭质层，使外界火源与基材隔绝，从而起到阻燃作用。通常以基料、发泡料、成炭剂、脱水成炭催化剂、防火添加剂、无机颜填料、辅助剂等制成。这类漆遇小火不燃，离火自熄，具有防延燃性。广泛应用于建筑、车辆、仓库、电器、包装等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。