2) porous iron matrix
多孔铁基体
3) quasipolygonal ferrite
准多边形铁素体
1.
When the finish cooling temperature was selected around 630?℃,a proper combination of quasipolygonal ferrite,granular bainite and fine M/A could be obtained.
冷却速度和终冷温度对最终组织类型和性能有很大影响,终冷温度控制在630℃,可得到准多边形铁素体、粒状贝氏体和细小M/A组元的混合组织,该类型组织屈服强度可达到600MPa,且具有较好的塑性和低温冲击性能。
4) YIG polycrystalline ferrite
YIG多晶铁氧体
1.
One of the development trends of microwave YIG polycrystalline ferrite material is wide band,low loss and high power material.
微波YIG多晶铁氧体材料的发展趋势之一是宽频带、低损耗、高功率材料。
5) multipurpose ferrite
多功能铁氧体
1.
A newly acoustical and vibration control devices combining multipurpose ferrites and magnetorheological fluids;
多功能铁氧体和磁流变液结合的新型声学与振动控制器件
6) quasi-polygonal ferrite
准多边形铁素体
1.
It is shown that the micro-alloyed steel possesses high strength and excellent low-temperature toughness due to a mixed microstructure of acicular ferrite and quasi-polygonal ferrite.
结果表明:基体组织为针状铁素体+准多边形铁素体的复合组织,该复合组织具有较高的强度和优异的低温韧性;两种组织之间的界面以及针状铁素体条束之间的界面均为大角晶界,能够对裂纹的扩展起到有效的阻碍作用,增加裂纹扩展功,使得F40级船板具有良好的低温韧性,-80℃的冲击功都可以达到138J以上。
2.
e acicular ferrite and quasi-polygonal ferrite,which the grain boundaries between them are large boundary.
通过 OM、SEM、TEM、EBSD 等手段研究了针状铁索体+准多边形铁素体的复合组织的 F40级船板钢的低温冲击韧性及其机理,由于这种复合组织之间界面均为大角晶界,晶界上存在大量被细小析出所钉扎的位错,对裂纹的扩展起到有效的阻碍作用,使得组织具有良好的低温韧性,-80℃的冲击功可以达到138J 以上。
3.
The optical microscope, SEM and TEM tests show that the final microstructure consists of fine grain size acicular ferrite or quasi-polygonal ferrite、pearlite and little granular bainite, etc.
通过光学显微镜、扫描电镜、透射电镜研究表明:最终组织为细小的针状铁素体或准多边形铁素体、珠光体及少量粒状贝氏体等组成的混合组织。