1) pitch-based ultrafine carbon fiber
沥青基超细碳纤维
2) pitch-based carbon fiber
沥青基碳纤维
1.
Super thermal conductive mesophase pitch-based carbon fibers;
超级导热型沥青基碳纤维
2.
The paper covered the uses of heavy aromatic oil in rubber softener,pitch-based carbon fiber,needle coke,surfatant,heat transfer fluid,etc through suitable processes.
通过适当的工艺,重质芳烃油可用于生产橡胶软化剂、沥青基碳纤维、导热油、针状焦、表面活性剂等。
3.
The production and application of pitch-based carbon fiber in the world are described and the development of pitch-based car-bon fiber is expected.
介绍了国内外沥青基碳纤维的生产应用情况,并对沥青基碳纤维的发展进行了展望。
4) pitch carbon fiber
沥青碳纤维
1.
The production capacity of the pitch carbon fiber is on a small scale, though the research in out country is carried out for a long time from the beginning, there are great gap compared with the foreign countries in the research and production application.
沥青碳纤维研制要经过原料沥青的精制,沥青的调制,而后形成沥青碳纤维原丝,沥青碳纤维原丝必须经过预氧化和碳化处理,才能成为工业可用的碳纤维丝。
5) nitrogen containing activated carbon fiber
含氮沥青基活性碳纤维
6) petroleum asphalt fiber
石油沥青基碳纤维
1.
The authors have made a microelectrode with the material of petroleum asphalt fiber.
作者研制了一种以石油沥青基碳纤维为电极材料的微电极,基于此种材料的特殊性能,经氧化处理后可获得较一般微电极为大的比表面积,困而其电流响应亦较一般微电极为大。
补充资料：沥青基超细碳纤维
分子式：
CAS号：
性质：由各向同性和中间相沥青经熔喷法制得的超细碳纤维及毡片。直径2～5μm，通用级可纺性好，但碳丝强度极低，高强型碳丝强度1.47GPa。模量147GPa。石墨丝最高强度3.14GPa。伸长率0.43％。模量735GPa，平均长度87mm。制法:(1)将通用级沥青在其熔点以上温度熔喷，制得毡片后稳定化和碳化而得；(2)将软化点为275～285℃的中间相沥青(含量95％～100％)，在310～320℃及360～370℃空气流下熔喷，用常规法连续不熔化和碳化(1400℃)，必要时在2500～2800℃石墨化而得。用作电磁波屏蔽材料、水泥和复合材料增强剂、活陛炭纤维、锂电池电极、制动材料及摩擦材料等。
CAS号：
性质：由各向同性和中间相沥青经熔喷法制得的超细碳纤维及毡片。直径2～5μm，通用级可纺性好，但碳丝强度极低，高强型碳丝强度1.47GPa。模量147GPa。石墨丝最高强度3.14GPa。伸长率0.43％。模量735GPa，平均长度87mm。制法:(1)将通用级沥青在其熔点以上温度熔喷，制得毡片后稳定化和碳化而得；(2)将软化点为275～285℃的中间相沥青(含量95％～100％)，在310～320℃及360～370℃空气流下熔喷，用常规法连续不熔化和碳化(1400℃)，必要时在2500～2800℃石墨化而得。用作电磁波屏蔽材料、水泥和复合材料增强剂、活陛炭纤维、锂电池电极、制动材料及摩擦材料等。