1) poly-p-vinylphenol
聚对乙烯基苯酚
2) Poly(p-vinylphenol)
聚(对-羟基苯乙烯)
3) poly (p-hydroxystyrene)
聚对羟基苯乙烯
1.
Especially,poly (p-hydroxystyrene) is emphatically de- scribed.
本文综述了248 nm KrF光致抗蚀剂成膜树脂的研究进展,重点介绍了聚对羟基苯乙烯及其衍生物,并简要介绍了其合成方法及成像机理。
4) PPMS
聚对甲基苯乙烯
5) poly(p-nitrostyrene)
聚对硝基苯乙烯
1.
Polystyrene(PS) powder was synthesized by emulsion polymerization,then poly(p-nitrostyrene)(PPNS) was prepared by nitration of PS using the mixture of nitric acid and sulfuric acid as nitrating agents,and finally PPNS was reduced to poly(p-aminostyrene)(PPAS) in the presence of stannous chloride and hydrochloric acid as reducing agent.
通过乳液聚合制备粉末状聚苯乙烯(PS),以浓HNO_3和浓H_2SO_4的混合酸为硝化试剂对PS进行硝化,制备了聚对硝基苯乙烯(PPNS),再以SnCl_2HCl为还原剂将PPNS还原为聚对氨基苯乙烯(PPAS)。
6) poly(p-aminostyrene)
聚对氨基苯乙烯
1.
Polystyrene(PS) powder was synthesized by emulsion polymerization,then poly(p-nitrostyrene)(PPNS) was prepared by nitration of PS using the mixture of nitric acid and sulfuric acid as nitrating agents,and finally PPNS was reduced to poly(p-aminostyrene)(PPAS) in the presence of stannous chloride and hydrochloric acid as reducing agent.
通过乳液聚合制备粉末状聚苯乙烯(PS),以浓HNO_3和浓H_2SO_4的混合酸为硝化试剂对PS进行硝化,制备了聚对硝基苯乙烯(PPNS),再以SnCl_2HCl为还原剂将PPNS还原为聚对氨基苯乙烯(PPAS)。
补充资料：聚对乙烯基苯酚
分子式：
CAS号：
性质：对乙烯基苯酚的聚合物。按聚合条件的不同，分子量可从数千到数十万，Mn1000～6000的聚合物，Mw/Mn=1.5～2.0，软化点160～200℃。相对密度1.2。白色粉末，主要用作环氧树脂的固化剂。
CAS号：
性质：对乙烯基苯酚的聚合物。按聚合条件的不同，分子量可从数千到数十万，Mn1000～6000的聚合物，Mw/Mn=1.5～2.0，软化点160～200℃。相对密度1.2。白色粉末，主要用作环氧树脂的固化剂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。