1) chrome-magnesite brick
铬镁砖
2) Magnesia-chrome brick
镁铬砖
1.
Destruction mechanism of magnesia-chrome bricks for different kinds of high-temperature furnace
不同类型高温窑炉用镁铬砖损毁机理分析
2.
This paper describes the influence of production condition of the dry-process cement rotary kiln on the service life of the magnesia-chrome brick.
为了实现我国大型干法水泥回转窑烧成带用直接结合镁铬砖的国产化,本文分析了干法水泥生产工艺条件对镁铬砖使用寿命的影响,总结了国外对镁铬砖损毁机理的研究结果,优化了水泥窑用直接结合镁铬砖的原料及生产工艺,研制出性能优异的大型干法水泥窑用直接结合镁铬砖LZMGe-8A。
3) alumina-magnesia-chrome refractory
铝镁铬砖
4) Magnesia chrome brick
镁铬砖
1.
Chemical property and detoxifcation of hexavalent chromium contained in magnesia chrome brick used in cement kiln;
水泥窑用镁铬砖中Cr~(6+)化合物的化学性质和解毒
5) MgO-Cr_2O_3 refractory
镁铬砖
1.
Effect of slag composition on the corrosion of MgO-Cr_2O_3 refractory used for RH lining;
预熔精炼渣组成对RH用镁铬砖侵蚀的影响
6) Magnesia chromite brick
镁铬砖
1.
Elimination of chrome-pollution and utilization of substitute fuels in cement kilns have been causing successful substitution of magnesia chromite brick by chromite-free basic bricks consisted of dolomite brick, magnesia spinel brick and magnesia zirconia brick.
消除铬公害和在水泥窑内应用代用燃料促使白云石砖、尖晶石砖和镁锆砖组成的系列无铬碱性砖成功地替代着镁铬砖。
补充资料：铬镁砖
分子式：
CAS号：
性质：与镁铬砖一样，是以尖晶石和方镁石为主晶相的耐火制品。性能介于铬质和镁铬质耐火材料之间。以铬矿和烧结镁砂为原料，按适当比例制成含氧化铬18％～30％，氧化镁25％～55％的复合碱性耐火砖。一般把铬矿加入量小于50％的称为镁铬砖，大于或等于50％的称为铬镁砖。其产品除了在弱氧化性气氛下烧成的烧结铬镁砖外，也可以制成不烧砖、熔铸砖、电熔再结合铬镁砖和散状料形态。可用于转炉、感应炉、有色金属冶炼炉的炉衬，电弧炉、平炉、均热炉的侧墙等。当铬矿与烧结镁砂的配比各为50％时，制品具有最大的抗热震性能，有时也称之为热震稳定性铬镁砖，主要用作碱性平炉顶砖。
CAS号：
性质：与镁铬砖一样，是以尖晶石和方镁石为主晶相的耐火制品。性能介于铬质和镁铬质耐火材料之间。以铬矿和烧结镁砂为原料，按适当比例制成含氧化铬18％～30％，氧化镁25％～55％的复合碱性耐火砖。一般把铬矿加入量小于50％的称为镁铬砖，大于或等于50％的称为铬镁砖。其产品除了在弱氧化性气氛下烧成的烧结铬镁砖外，也可以制成不烧砖、熔铸砖、电熔再结合铬镁砖和散状料形态。可用于转炉、感应炉、有色金属冶炼炉的炉衬，电弧炉、平炉、均热炉的侧墙等。当铬矿与烧结镁砂的配比各为50％时，制品具有最大的抗热震性能，有时也称之为热震稳定性铬镁砖，主要用作碱性平炉顶砖。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条