1) palladium-silver-gold-nickel alloy
钯银金镍合金
2) Pd-Ni alloy
钯镍合金
1.
Cyclic Voltammetry (CV) was used to study the electrochemical conditions in order to synthesize nanowires of Pd-Ni alloy in the mixtures composed of PdCl 2 and NiSO 4.
用循环伏安法对NiSO4 与PdCl2 混合溶液合成钯镍合金纳米线的电化学沉积条件进行了研究 。
2.
The effects of Ni/Pd ions mass ratio, pH value, current density, electrodeposition potential and other process parameters on the composition of low-speed electrodeposited Pd-Ni alloy are discussed.
讨论了钯镍浓度比、pH值、电流密度、沉积电势等工艺参数对低速电沉积钯镍合金组成的影响。
3) nickel palladium alloy
镍钯合金
4) palladium-nickal alloy
钯-镍合金
5) gold-palladium-nickel alloys
金钯镍合金
6) Pd-Ag alloy
钯-银合金
1.
Rare earth improved electroless plating method was developed for simultaneously depositing Pd-Ag alloy film on ceramic support.
采用稀土改进的化学镀法在多孔陶瓷载体上共沉积钯-银合金膜。
补充资料：钯银金镍合金
分子式：
CAS号：
性质：是钯基含银、金和镍的四元合金，少量镍可提高合金在氢中的热稳定性。有PdAgAuNi23-3-0.3和PdAgAuNi23-3-1两种合金。它们的室温抗拉强度分别为726MPa和765MPa，450℃时分别为569 MPa和596 MPa。原子比（H/Me）分别为0.35和0.34。PdAgAuNi23-3-0.3合金的透氢速度（450℃）13.3cm3/(cm2·min)。生产方法参见钯银合金。高纯氢净化材料，使用寿命比较长。
CAS号：
性质：是钯基含银、金和镍的四元合金，少量镍可提高合金在氢中的热稳定性。有PdAgAuNi23-3-0.3和PdAgAuNi23-3-1两种合金。它们的室温抗拉强度分别为726MPa和765MPa，450℃时分别为569 MPa和596 MPa。原子比（H/Me）分别为0.35和0.34。PdAgAuNi23-3-0.3合金的透氢速度（450℃）13.3cm3/(cm2·min)。生产方法参见钯银合金。高纯氢净化材料，使用寿命比较长。