1) trimetaphosphate M(PO3)3(III)
三偏磷酸盐
2) metaphosphate
[英][,metə'fɔsfeit] [美][,mɛtə'fɑsfet]
偏磷酸盐
1.
Determination of phosphate,pyrophosphate,metaphosphate and total phosphorus in seafoods by ion chromatography
离子色谱法测定海产品中磷酸盐、焦磷酸盐、偏磷酸盐和总磷
2.
The crystals are grown from aqueous solution doped with a minute amount of sodium metaphosphate.
掺杂微量偏磷酸盐即可使KDP晶体中出现散射颗粒 ,随着掺杂浓度提高 ,散射颗粒密度增大。
3.
The results of differential thermal analysis on glasses show that the glass forming ability was improved greatly by introducing metaphosphate to AMCSBY glass.
对玻璃进行了差热分析 ,结果表明 ,在氟铝酸盐玻璃中引入偏磷酸盐使玻璃形成能力大大提高 ;测量了玻璃从紫外到红外的透过光谱和紫外吸收光谱 ,在玻璃中引入偏磷酸钡使玻璃中红外透过能力下降 ,红外吸收边带移向短波段 ,玻璃紫外透过能力得到提高。
3) triphosphate
[英][trai'fɔsfeit] [美][traɪ'fɑs,fet]
三磷酸盐
4) tetrametaphosphate
四偏磷酸盐
5) metaphosphite
偏亚磷酸盐
6) hexametaphosphate
六偏磷酸盐
1.
A series of micro-arc oxidation(MAO) layers was produced on the surfaces of die cast magnesium alloy AZ91 in hexametaphosphate electrolyte.
采用六偏磷酸盐体系在AZ91压铸镁合金表面制备了一系列微弧氧化膜层。
补充资料：三偏磷酸盐
分子式：
CAS号：
性质：由三个PO43—四面体通过共用氧原子联接在一起。易溶于水。典型的是三偏磷酸钠Na(PO3)3。白色结晶或结晶性粉末。可由水合磷酸二氢钠于110℃时脱水成无水盐，再加热至162℃成焦磷酸二氢钠，再加热至162℃成焦磷酸二氢钠，再加热到237℃而制得。在327℃或更高的温度下加热得聚磷酸盐(OP(ONa)O)3x，碱过量时产生线型聚磷酸盐—OP(ONa)O—OP(ONa)O—，碱量不足时生成链与链之间带侧链的二聚物，碱性水解生成四聚磷酸盐P4O10—5。三偏磷酸盐可用作淀粉改性剂、保水剂、水质软化剂、分散剂、肉类黏结剂（能防止食品变色）。
CAS号：
性质：由三个PO43—四面体通过共用氧原子联接在一起。易溶于水。典型的是三偏磷酸钠Na(PO3)3。白色结晶或结晶性粉末。可由水合磷酸二氢钠于110℃时脱水成无水盐，再加热至162℃成焦磷酸二氢钠，再加热至162℃成焦磷酸二氢钠，再加热到237℃而制得。在327℃或更高的温度下加热得聚磷酸盐(OP(ONa)O)3x，碱过量时产生线型聚磷酸盐—OP(ONa)O—OP(ONa)O—，碱量不足时生成链与链之间带侧链的二聚物，碱性水解生成四聚磷酸盐P4O10—5。三偏磷酸盐可用作淀粉改性剂、保水剂、水质软化剂、分散剂、肉类黏结剂（能防止食品变色）。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。