1) hot forming
大火成形
2) flame formation
火焰形成
3) line heat forming
水火成形
4) one-heating forming
一火成形
1.
Based on the theory of the hot-forging forming, the work is introduced in the research on the 6700 steering knuckle of light truck as follows:(1) Based on the friction press for forming equipment, designing a forging process of one-heating forming, i.
本文根据热锻成形理论,以6700轻卡汽车转向节为研究对象,做了以下工作:(1)以摩擦压力机为锻造成形设备,设计了一火成形锻造工艺,即下料→中频加热→制坯→预锻→终锻。
5) Shaping hardening machine
成形淬火机
1.
Based on the processing technological needs of steel board springs,this paper mainly introduced the selection,design and calculation of transmission plan,overall design and electric control design of the shaping hardening machine,etc.
本文根据板簧的加工工艺要求,主要介绍板簧成形淬火机的传动方案选择及设计计算、总体设计和电气控制设计等内容,实际可行。
6) Electric Spark Forming
电火花成形
1.
Research on Electric Spark Forming Method for Low-Rigidity Thin-Long Shafts;
低刚度细长轴的电火花成形方法研究
补充资料：主要射出成形材料成形时应注意事项
■主要射出成形材料成形时应注意事项
品 名 注 意 事 项
PVC
聚氯乙烯
1. 产品种类范围非常广（硬质、软质、聚合物等），成型条件各有不同，从熔融至分
解之温度范围很小，尤须注意加热温度。
2. 附着水分少，但成型周期尽可能减少（50℃~60℃热风干燥）。
3. 成型机方面，与材料直接接触的部位须电镀或采用不锈钢以防热分解所产生的盐酸
侵蚀。射出压力2100kg/cm2程度。
4. 所有塑料当中必须是细心注意温度调节。
5. 浇口附近易产生流纹，故射出操作后，柱塞不要后退使浇口充分固化后再瞬间退后为宜。
6. 加热之初温不宜高，特别注意熔融情形。第二级加热温度较高，且尽可能使成形周
期缩短，比较安全。
PA
聚醯胺树脂
1. 成型温度比其它材料高，故采用油加热的成形机较适当。
2. 吸湿性大，必须充分干燥。水分对成型品的品质影响甚大（80℃热风干燥约5~6小时）。
3. 须退火以消除内部歪斜。
PP
聚丙烯
1. 同PE，但成形温度必须较高。熔融温度170℃，超过190℃则流动性大增，则毛边增加，
易产生接缝及凹入情形。
PC
聚碳酸脂
1. 吸湿性比尼龙小，但若有些微之水分存在则成型品产生其它色泽或气泡，故必须密封
干燥同时成形时也须预备干燥（120℃之温度4小时）。
2. 加热温度超过320℃时则产生热分解，成品变色，故特别注意温度调节，又成型时的温度调节也非常重要，须特别注意其最低温度、最低时间。
3. 须退火以消除内部歪斜（130℃~135℃，1小时程度为准）。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。