1) corrosion cycle test
腐蚀循环试验
2) cyclic corrosion test
循环腐蚀试验
1.
By use of solventborne coatings and waterborne coatings,the influence of NORSOK M-501 cyclic corrosion test,ASTM B117 salt spray test,ASTM 5894 cyclic corrosion test and ASTM 5894 salt spray test on coatings have been studied.
分别采用溶剂型涂料和水性涂料体系,考察了NORSOK M-501循环腐蚀试验、ASTM B117盐雾试验、ASTM 5894循环腐蚀试验和单独的ASTM 5894盐雾试验对涂层的影响。
3) synergistic accelerated corrosion test
循环加速腐蚀试验
1.
By means of synergistic accelerated corrosion test and electrochemical measuring,the corrosion behavior of copper-stainless steel composites and Cu in HSO_(3)~(-)/Cl~- media was studied.
通过循环加速腐蚀试验和电化学测试方法,研究了3种铜-不锈钢复合材料和纯铜在HSO3-和/或Cl-介质中的腐蚀行为。
5) Immersion-wet-dry cycle accelerated corrosion test
浸渍干湿循环加速腐蚀试验
6) cyclic corrosion
循环腐蚀
1.
Two kinds of carbon fiber/epoxy composites were studied under cyclic corrosion conditions of light radiation-humidity.
采用仿自然环境的氙灯光照-加湿的循环腐蚀条件对两种碳纤维/环氧树脂复合材料进行了腐蚀试验,结果表明两种材料的表面发生了严重的腐蚀,单排复合材料的力学性能发生了明显的降低,编织复合材料的力学性能变化不大,FT-IR测定表明材料表面可能发生了光化学反应。
补充资料：缝隙腐蚀试验
缝隙腐蚀试验
crevice corrosion test
fengx}fush{shlyan缝隙腐蚀试验(creviee。orrosion test)评价缝隙腐性性能的金属腐性试验方法。它可分为电化学法和化学浸泡法。(1)电化学方法:利用人造缝隙测量其去钝化pH值或缝隙内的电位，以评定材料耐缝隙腐蚀性能。(2)化学浸泡法:以腐蚀失重或深度为基准来评定材料耐缝隙腐蚀性能的一种方法。试样的制备方法很多，有的把沙土或碎石块堆积在金属板上，有的用橡胶带把金属缠起来等，常用的有三氯化铁腐蚀法和快速缝隙腐蚀试验方法。三氯化铁缝隙腐蚀试验方法的中国国家标准为GBlo127一88，主要适用于不锈钢和镍一铬合金。该试验是把按要求制成的带有缝隙的试样浸入到10%FeCI:·6HZO溶液中，测量浸泡一定时间后的腐蚀深度或失重量。快速缝隙腐蚀试验法是用两块面积不等的金属试片构成一个人造缝隙，浸放到3%NaCI+。.肠MNaZSO;十活性炭的腐蚀溶液中，温度控制在3Q〔C或60C，不断吹入氧气，待一定时间后取出进行清洗、称量。此外，还有现场浸泡法。它是把带有缝隙的试样浸入到现场介质中，待一定时间后取出称量，根据失重量来评价材料耐缝隙腐蚀的性能。 (李德林)