1) solution strengthening
固溶强化<冶>
2) solid solution strengthening
固溶强化
1.
Explanation based on electron theory for solid solution strengthening in copper alloy;
铜合金固溶强化的电子理论解释
2.
solid solution strengthening, strain hardening, grain boundaries strengthening, dispersion strengthening, etc and the investigations on strengthening mechanism are reviewed.
回顾和总结固溶强化、形变强化、晶界强化及弥散强化等常用铂强化方法及其强化机制的研究进展 ,介绍典型强化铂材料如铂铑合金、ZGSPt(Pt Rh)、ODSPt(Pt Rh)和DPHPt(Pt Rh)等弥散强化材料的主要性能和用途 ,为选择和开发更好的铂强化方法、推动强化铂的应用提供参考。
3.
One was called solid solution strengthening,i.
经过试验,总结出两种强化方法:一是固溶强化,通过添加高熔点的W,Mo元素,形成合金化固溶体,从而提高了材料的高温蠕变性能;二是时效强化,通过加入C和Zr元素生成碳化物强化相,并研究C,Zr元素含量、热处理工艺及压力加工方法对时效强化的影响,分析得知,C含量控制在0。
3) solid-solution strengthening
固溶强化
1.
The valence electron structure of solid-solution and solid-solution strengthening;
固溶体的价电子结构与固溶强化
2.
The alloy strengthening mechanisms of solid-solution strengthening,distortion strengthening,fine-grain strengthening and deposition strengthening have been reviewed.
简要介绍了固溶强化、形变强化、细晶强化和沉淀强化的强化机理。
4) solution strengthening
固溶强化
1.
The dissolution of the intermetallic phases was studied and the function of solution strengthening in Al-Si-Cu-Mg casting alloys during solution heat treatment was analyzed.
结果表明:在固溶处理初期,组织中θ相的数量逐渐减少,但在(FeMn)3SiAl12相中还有一定的Cu含量;而固溶后期,富铁相中的Cu含量也明显降低,且难溶的Al3Ti针状相也发生钝化,但部分Q相尚存在;随着固溶时间的延长,合金基体中Cu和Mg的含量逐渐增多,且富Mn和富Ti相也在合金基体中略有溶解;合金的固溶强化作用主要来源于富Cu相的溶解。
2.
It is thought that solution strengthening and second phase strengthening are two main ways for improving mechanical properties of magnesium alloy.
认为固溶强化和第二相强化是加入合金元素强化镁合金的主要方式。
3.
The results show that the minimum creep rate of the alloy decreases by two to ten times, creep stress increases by 50 MPa～150 MPa, such an excellent creep resistance results from solution strengthening of high niobium alloying and precipitate strengthening of carbide
2 B合金最小蠕变速率降低 2倍～ 10倍 ,蠕变应力提高 5 0 MPa～ 15 0 MPa,如此优越蠕变抗力主要来自于高铌合金化对钛铝合金的固溶强化及间隙原子的沉淀强
5) solution strength
固溶强化
1.
The result shows that the solution strength effect of yttrium is better than that of aluminum and the reason is the enhan.
对比Mg Al合金,阐明了Y优于Al在镁合金中的固溶强化作用的电子理论依据是键能得到增强;同时用电子理论解释了Mg24Y5中间相在镁合金中具有显著强化作用的原因是Y原子占据八面体中心位置,Mg-Y键有效强化了合金基体。
6) solutionizing
强化固溶
1.
The effect of promotively-solutionizing treatment on the mechanical properties and fracture of ultra high strength 7055 aluminum alloys;
强化固溶对7055铝合金力学性能和断裂行为的影响
2.
The effects of promotively-solutionizing of soluble remaining constituent phases on the microstructure and mechanical properties of 7075 and 7055 alloys were studied.
研究了强化固溶对提高７０７５和７０５５铝合金力学性能的效果。
补充资料：高温人合金固溶强化
高温人合金固溶强化
solid solution intensification of superalloy
gaowen hej*n gurong qlonghua高温合金固溶强化(solid solution intensifi-eation of superalloy)添加一些合金元素(即溶质元素)到铁、镍或钻基高温合金中，但仅形成单相奥氏体，达到高温合金强化的目的。溶质元素的作用主要是弹性交互作用、化学交互作用和电子交互作用。溶质原子使固溶体基体点阵发生畸变，使固溶体中滑移阻力增加而强化。有些溶质原子可以降低合金系的层错能，提高位错分解的倾向，导致交滑移难于进行，合金被强化。另外，强化作用还取决于溶质元素在周期表中的位置，即与溶质元素的电子空位数有关。这几种强化作用在温度不高于0.6T熔(合金熔点的绝对温度)时是相当重要的。在高温使用条件下(T)。.6T动，溶质元素是通过原子结合力提高，降低固溶体中元素的扩散能力，提高合金再结晶温度，阻碍扩散式形变过程而使合金得到强化。不同金属元素的自扩散系数及其热强性都是按钨、钥、担、妮、铬、镍、钻、铁、钦、铝的次序递减。100。℃使用的镍基合金固溶强化时飞扩散因素显得特别重要，钨的强化效果要优于钥;而能大量固溶的钻通过降低堆垛层错能对高温强度做出很大贡献。在高温合金固溶强化时，采用多元合金化能更好地提高热强性效果，这也与进一步降低基体中元素的扩散过程有关。固溶强化的效果不仅与所加入元素本身的单位强化效应有关，而且还与元素的加入量有关，在溶解度范围内应尽可能的大量加入固溶元素，使固溶强化作用充分发挥。周期表中第班族元素铬、钥、钨具有大的溶解度和良好的固溶强化效果。第v族元素中特别是妮、担也具有不小的溶解度，与铬、钥、钨一样，在高温时可以有效地降低扩散过程，以及通过降低堆垛层错能来增加扩张位错的宽度，以阻碍高温蠕变时位错的主要合金元素的固溶强化作用。攀移或交滑移的进行，达到显著的强化效应。表中列出 主要合金元素的固溶强化作用公异片一 注:(+)有利作用;(一)不利作用;(·)无一定作用。