1.
It has been discovered and demonstrated, via scanning electron microscope examination on 6 samples of broken glasses, that one important cause for the spontaneous breakage in tempered glass occurs as a result of the single-phase polycrystalline silicon particles, rather than simply the nickel sulfide (NiS) particles that are commonly recognized to be the main cause for the spontaneous breakage.
通过对 6 块玻璃自爆残片的电镜观察和成分分析,发现并证明了引起钢化玻璃自爆的主要原因不仅仅是传统认识中的硫化镍(NiS)微粒,很多情况是由单质硅微粒引起的。
2.
The causes of bend and distortion of tempered glass were discussed and some solutions were also suggested under any circumstances.
分析了钢化玻璃变形弯曲的原因,提出了各种情况下解决钢化变形的方法。
3.
Beijing Botanical Garden Exhibition Greenhouse uses point type glass curtain wall with imported tempered glass from French.
北京植物园展览温室采用点式玻璃幕墙 ,其钢化玻璃均从法国进口 ,抗弯强度和弹性模量能否采用现有的中国幕墙规范数值是个问题。
5) toughened glass
钢化玻璃
1.
Experimental study on the effect of toughened glass protected by window type sprinkler;
窗型玻璃喷头对钢化玻璃保护效果的实验研究
2.
Experimental study on the effect of single-pane toughened glass protected by water sprinkler as fire barrier;
喷水保护单片钢化玻璃作为防火分隔的有效性实验研究
3.
The article describes the problem of the toughened glass' surface defect and the method of prevention and solution.
针对钢化玻璃表面质量存在的变形点缺陷,采取相对应措施预防和解决。
6) glass tempering furnace
玻璃钢化炉
1.
On the base of heat transfer theory and glass tempering furnace industrial application,the two practical mathematic models of plane and roll are established,and the image simulation of calcution result is done.
在综合传热理论和玻璃钢化炉实际操作经验的基础上,建立了具有实用意义的玻璃板和传动辊传热数学模型;并对计算结果分别进行图像模拟。
2.
The ceramic roller is one of the key components in the glass tempering furnace.
陶瓷辊道是玻璃钢化炉中的关键部件,阐述了其设计、安装、使用及保养中应注意的问题,并对如何延长其使用寿命提出了一些切实可行的建议。
3.
It described how to design t he belt driving in the glass tempering furnace, and some problems in production.
阐述了玻璃钢化炉中,皮带传动的设计和在生产中需要注意的问题。
补充资料：钢化玻璃
| 钢化玻璃 toughened glass 经强化处理、具有良好机械性能和耐热振性能的玻璃制品。主要用于汽车、火车、船舶、建筑物、器皿、仪表、家具等方面。钢化玻璃的制作工艺可以分为物理钢化和化学钢化两大类。物理钢化是将玻璃加热到接近软化温度，随即用冷却介质快速冷却，使玻璃表面产生压应力。按其冷却介质的不同，可以分为风冷钢化、液冷钢化和固冷钢化。其制品有平钢化玻璃、弯钢化玻璃、半钢化玻璃、区域钢化玻璃、器皿钢化玻璃、仪表用钢化玻璃等。物理钢化玻璃具有较高的抗弯强度、抗冲击强度和抗热振性能，破碎后，其碎片不带尖锐棱角，而是聚在一起成为布满裂缝的集合体，可减少对人的伤害。但物理钢化玻璃不能进行机械切割和钻孔，有自爆等特性。化学钢化是用化学方法改变玻璃表面组分以增加玻璃机械强度和耐热振性。其工艺过程是：在一定温度下，把玻璃浸入熔盐中，玻璃中的碱离子与熔盐中的碱离子因扩散而发生离子交换，使玻璃表面产生压应力，从而提高玻璃的机械强度和抗热振性能。可分为低温和高温两种类型，适用于薄壁、异型和要求尺寸精确的玻璃制品。 |