1) bulk factor of molding compound
模塑料压缩比
2) IMC
注射-压缩模塑料
3) compression molding
压缩模塑
1.
The compression molding process of such long fiber reinforced PP was investigated.
采用粉末浸渍的方法制备连续玻璃纤维增强聚丙烯预浸料,经切割获得长纤维增强聚丙烯粒子,采用单螺杆挤出机挤出形成模塑料,探索了模塑料的压缩模塑成型工艺,研究了成型后材料的力学性能及其影响因素。
2.
A mathematical model of heattransfer in partwas established to simulate thermalbehav- ior of GMT parts during compression molding,coupled with non- isothermal crystallization kinetics of polypropylene.
采用有限元方法 ,对 PP/ GMT制品压缩模塑的冷却与结晶过程进行数值模拟 ,采用非等温结晶模型 ,计算出不同条件下制品中树脂的结晶度和制品内部温度分布 ,并与实验结果进行了对比 ,为压缩模塑中保压冷却时间的确定提供了理论依
3.
The effect of matrix resin,architecture and property of reinforcement,blank design,mold temperature and blank preheat temperature on the fiber distribution during compression molding of glass mat reinforced polypropylene(GMT-PP)was investigated by measuring the fiber content in various areas of GMT-PP after squeezing flow.
通过测定玻璃纤维毡增强聚丙烯经挤压流动后不同区域的纤维含量 ,研究了基体树脂、增强材料的结构与性质、坯料设计、模具温度及坯料的预热温度等对玻璃纤维毡增强聚丙烯在压缩模塑流动过程中纤维分布的影响。
4) compression mould
压缩塑模
6) inject-compression mould
注塑-压缩模
补充资料：注射-压缩模塑料
分子式：
CAS号：
性质：注射-压缩模塑用不饱和聚酯模塑料。ZMC不表示实在含义，包含三层意义——模塑料、注射模塑机械、模具。由于使用注射-压缩模塑成型，对玻纤破坏性小，定向性也小，制品机械强度(尤其是冲击强度)明显高于BMC。以汽车面板为例，冲击强度较BMC注射产品提高117％，弯曲弹性模量提高38％，弯曲强度提高5％(两种模塑料的玻纤含量均为25％)。ZMC的玻纤长度一般为25mm，类似于BMC。生产速度明显高于SMC。主要用于注射-压缩成型。
CAS号：
性质：注射-压缩模塑用不饱和聚酯模塑料。ZMC不表示实在含义，包含三层意义——模塑料、注射模塑机械、模具。由于使用注射-压缩模塑成型，对玻纤破坏性小，定向性也小，制品机械强度(尤其是冲击强度)明显高于BMC。以汽车面板为例，冲击强度较BMC注射产品提高117％，弯曲弹性模量提高38％，弯曲强度提高5％(两种模塑料的玻纤含量均为25％)。ZMC的玻纤长度一般为25mm，类似于BMC。生产速度明显高于SMC。主要用于注射-压缩成型。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。