1) mar-resisatant,scratch proof
![点击朗读](/dictall/images/read.gif)
耐刮的
2) scratch resistance
![点击朗读](/dictall/images/read.gif)
耐刮伤性
1.
After being added in the wood coatings,the wax particles were homodispersed in the coating films,which could improve the tackiness resistance and the scratch resistance of coating films.
采用复配法将水性蜡助剂加入到水性木器涂料中,蜡助剂在涂料成膜时均匀地分散在整个涂层中,蜡助剂的加入能够显著提高漆膜的抗回粘性和耐刮伤性能,但是大粒径的蜡助剂会引起漆膜光泽的下降。
2.
The morphology and structure of the nanocomposite coatings were characterized by transmission electron microscopy(TEM) and small angle X-ray scattering(SAXS) method,while the scratch resistance by the gloss loss of the coatings film after washing.
以四乙氧基硅烷(TEOS)作为主要前驱体,通过改变溶胶-凝胶工艺参数制得了结构和形态各异的丙烯酸酯聚氨酯/SiO2纳米复合涂层,利用TEM、SAXS等手段表征涂层的结构与形态,由洗刷前后涂层的失光率来表征耐刮伤性,详细探讨了纳米复合涂层耐刮伤性与SiO2相特征、有机无机相作用力及SiO2质量分数之间的关系。
3) scratch-resistant
![点击朗读](/dictall/images/read.gif)
耐刮擦
1.
The mechanical properties and scratch-resistant properties of PC/ABS alloys could be improved obviously by adding nano-MgO particles.
添加纳米MgO后的PC/ABS合金与纯PC/ABS空白样相比,其拉伸、弯曲和缺口冲击强度及表面耐刮擦性能都得到了明显改善,其中合金弯曲强度可提高20%,缺口冲击强度可提高77。
2.
The scratch-resistant SiO2 antireflective coatings were prepared by dipping of the glass followed by a thermal curing at 700 ℃ taking place simultaneously with the glass toughening, using the base/acid two-step catalytic sol-gel process with tetraethylorthosilicate (TEOS) as precursor.
17%,在400-800nm的波长范围内平均反射率较镀膜前下降了5%以上,同时薄膜具有较好的耐刮擦性能。
4) scratch resistant coatings
![点击朗读](/dictall/images/read.gif)
耐刮伤涂层
1.
Organic-inorganic nanocomposite scratch resistant coatings for polycarbonate(PC)were successfully fabricated by evaporation induced self-assembly method.
利用挥发诱导自组装法制备了聚碳酸酯(PC)有机-无机纳米复合耐刮伤涂层,考察了基材处理方式、自组装液组成、涂装工艺等因素对自组装涂层厚度、透明性及耐刮伤性的影响。
5) scratch-resistant property
![点击朗读](/dictall/images/read.gif)
耐刮擦性能
6) applicable by spatula
![点击朗读](/dictall/images/read.gif)
可刮的
补充资料:光敏耐腐蚀耐电镀印料
分子式:
CAS号:
性质:系指通过紫外光照射固化的一类抗蚀印料,分为:(1)耐腐蚀型,稀碱溶液去膜,能耐酸性腐蚀;溶剂去膜,能耐酸及碱腐蚀。(2)耐电镀抗蚀型,稀碱溶液去膜,耐酸性电镀液,溶剂去膜,耐弱碱性、酸性电镀液;(3)堵孔型印料,碱溶;(4)加强抗蚀型,去除型(耐化学镀铜)和永久覆盖型。由碱溶性感光高分子树脂、光敏引发剂、活性稀释剂、触变剂、流平剂、着色剂等组成。将上述组分在预混合器中进行搅拌混合,再经三辊机碾磨后配制成产品。无溶剂,无气味,不污染环境,很少有针孔。在印刷中黏度不变化,具有良好的丝网印刷性能。稀碱溶液去膜,能耐三氯化铁、氯化铜、过硫酸铵等酸性蚀刻,耐硫酸铜、铅锡合金及金银等酸性电镀液腐蚀。用于丝网图形蚀刻法和图形电镀法制造印制电路图形,也可用于化学蚀刻法制造精密的金属零件和图形。
CAS号:
性质:系指通过紫外光照射固化的一类抗蚀印料,分为:(1)耐腐蚀型,稀碱溶液去膜,能耐酸性腐蚀;溶剂去膜,能耐酸及碱腐蚀。(2)耐电镀抗蚀型,稀碱溶液去膜,耐酸性电镀液,溶剂去膜,耐弱碱性、酸性电镀液;(3)堵孔型印料,碱溶;(4)加强抗蚀型,去除型(耐化学镀铜)和永久覆盖型。由碱溶性感光高分子树脂、光敏引发剂、活性稀释剂、触变剂、流平剂、着色剂等组成。将上述组分在预混合器中进行搅拌混合,再经三辊机碾磨后配制成产品。无溶剂,无气味,不污染环境,很少有针孔。在印刷中黏度不变化,具有良好的丝网印刷性能。稀碱溶液去膜,能耐三氯化铁、氯化铜、过硫酸铵等酸性蚀刻,耐硫酸铜、铅锡合金及金银等酸性电镀液腐蚀。用于丝网图形蚀刻法和图形电镀法制造印制电路图形,也可用于化学蚀刻法制造精密的金属零件和图形。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。
参考词条