1) nickel-zinc ferrite crystal
镍锌铁氧体晶体
2) Ni-Zn ferrite
镍锌铁氧体
1.
Preparation of Ni-Zn ferrite from sodium jarosite residue;
用黄钠铁矾渣制备复合镍锌铁氧体
2.
The relationship between magnetization differential and temperature in Ni-Zn ferrite;
镍锌铁氧体微分磁化率与温度的关系
3.
The relations of magnetization differential with magnatic intensity describedby dM/dt-H curves are studied in Ni-Zn ferrite with a constant rate of increasing H.
用匀速率增加的直流磁场Ｈ磁化不同居里温度的镍锌铁氧体试样，测得磁化强度Ｍ的时间变化率曲线表明：同一温度下随外场速率Ｈ增加，曲线升高；同一外场速率下随温度升高，曲线降低；微分磁化率ｄＭ／ｄＨ可以采用等效畴壁运动表示。
3) nickel-zinc ferrite
镍锌铁氧体
1.
Micropore and nanosized nickel-zinc ferrite particle was prepared from nickel sulfate, zinc sulfate and ferric sulfate with spasmolytol and polyethylene glycol as the template by hydrothermal template process.
以镍、锌、铁的硫酸盐为原料、三乙胺和聚乙二醇作为模板剂,采用水热模板法制备了纳米镍锌铁氧体粉体,并通过红外光谱分析(FT-IR)、X射线衍射(XRD)、比表面积检测(BET)、扫描电镜(SEM)、密度测量等手段对样品进行表征。
4) NiZn ferrite
镍锌铁氧体
1.
Nano-NiZn ferrite, nano-Ba ferrite and nano-NiZnCu ferrite were produced by sol-gel method and their properties were measured.
本文采用溶胶-凝胶法制备了纳米镍锌铁氧体，纳米钡铁氧体，纳米镍锌铜铁氧体三种微波吸收剂并对其特性进行了研究。
2.
In this paper, NiZn ferrites have been prepared using solid-state mixing method.
本文采用氧化物混合工艺制备镍锌铁氧体。
5) Ni-Zn ferrite
镍-锌铁氧体
6) nickel zinc ferrite
镍锌铁氧体
1.
Nanosized nickel zinc ferrite(Ni0.
用水热法分别在200℃和220℃下反应5h制备了纳米级镍锌铁氧体(Ni0。
补充资料：镍锌矩磁铁氧体
分子式：Ni-Zn
CAS号：
性质：具有矩形磁滞回线、尖晶石型结构的铁氧体。化学式为（NiO、ZnO）Fe2O3。矫顽力238.0～557.2A/m。在20～70℃的范围内矫顽力的变化率小于5%。矩形比0.8左右。居里温度200～300℃，介电常数约12.5。体积电阻率5×104Ω·cm。主要原料为镍、锌和铁的氧化物。少量改性添加剂为铜、锰、镁、钴等的氧化物。采用电子陶瓷工艺制造，但要进行磁热处理。处理前磁滞回线一般呈蜂腰状，处理后为矩形。其优点是温度稳定性好，输出信号大，而缺点是生产工艺较复杂，开关时间较长，输出波形一致性较差。可作为天线棒、调谐插头、记忆元件、开关元件、逻辑元件、磁放大器，磁光存储器及磁声存储器等。
CAS号：
性质：具有矩形磁滞回线、尖晶石型结构的铁氧体。化学式为（NiO、ZnO）Fe2O3。矫顽力238.0～557.2A/m。在20～70℃的范围内矫顽力的变化率小于5%。矩形比0.8左右。居里温度200～300℃，介电常数约12.5。体积电阻率5×104Ω·cm。主要原料为镍、锌和铁的氧化物。少量改性添加剂为铜、锰、镁、钴等的氧化物。采用电子陶瓷工艺制造，但要进行磁热处理。处理前磁滞回线一般呈蜂腰状，处理后为矩形。其优点是温度稳定性好，输出信号大，而缺点是生产工艺较复杂，开关时间较长，输出波形一致性较差。可作为天线棒、调谐插头、记忆元件、开关元件、逻辑元件、磁放大器，磁光存储器及磁声存储器等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。