1) zong of late wood
晚材带
3) autumn wood
晚材，秋材
4) latewood percent
晚材率
1.
93 15-year-old trees from the 31 provenances trial stand in Nanyu Forest Farm of Fujian Province were collected to deal with variations in bending properties of wood (modulus of elasticity and modulus of rupture) for exotic Loblolly Pine (Pinus teada) and their relationships to trees age, latewood percent and wood density in this paper.
树龄、晚材率和木材密度与MOE、MOR在0。
5) Late wood percentage
晚材率
1.
Wood anatomy of 12-13 year old Chinese fir plantation in different growth environments (south hillside, mountain valley, ridge, mountain top) was studied by measuring annual ring width, late wood percentage, tracheid length, tracheid width, thickness of cell wall, ratio of length to width, ratio of cell wall to cavity, microfibrillar angle, proportion of wood tissues, air-dried density.
本文采用宏观和微观方法，以木材的年轮宽度及晚材率，管胞形态因子，微纤丝角，组织比量，气干密度为指标，对不同生长环境(南坡，山谷，山脊，山顶)的人工林杉木(12——13年生)的木材解剖特征进行研究，结果表明：(1)不同生长环境全树间的年轮宽度及晚材率均达到了差异显著水平，其大小顺序为，年轮宽度：山谷(7。
6) late wood ratio,late wood percentage;percent of late wood
晚材率(林)
补充资料：板带材
宽厚比很大的矩形断面金属材，主要用轧制方法生产，用途极为广泛。板带材可根据需要剪裁、弯曲、冲压和焊接成各种构件和制品。高速连续式的板带轧机和宽厚板轧机的迅速发展，使板带材成本降低，质量提高，应用日益广泛。工业发达国家的板带钢产量在钢材总产量中的比重逐年增加，目前已达60％左右。
用轧制方法生产的板带材中，最薄的箔材厚度仅有0.001mm,最厚的板材厚度约为300mm；宽度最窄的为1mm，最宽达5300mm。板带材除按钢种和有色金属牌号分类外，一般还按尺寸分类,钢板厚度4mm以上的称中厚板。在中国习惯上称 4～20mm厚的板材为中板，20mm以上称厚板，60mm以上称特厚板(初轧板坯除外)。而对0.1～4mm的冷轧和热轧板带，单片的称薄板，成卷的称带钢。宽度在650mm以上的称宽带钢,不足650mm的称窄带钢。厚度4～60mm,宽度在200mm以下的热轧钢材在中国称扁钢。0.02～0.1mm的冷轧带称薄带。0.02mm以下的带材称箔材,钢铁箔材习惯称为超薄带。关于板带材的制造方法，见中、厚板轧制，带钢热轧，薄板叠轧，带钢冷轧，箔材轧制。
用轧制方法生产的板带材中，最薄的箔材厚度仅有0.001mm,最厚的板材厚度约为300mm；宽度最窄的为1mm，最宽达5300mm。板带材除按钢种和有色金属牌号分类外，一般还按尺寸分类,钢板厚度4mm以上的称中厚板。在中国习惯上称 4～20mm厚的板材为中板，20mm以上称厚板，60mm以上称特厚板(初轧板坯除外)。而对0.1～4mm的冷轧和热轧板带，单片的称薄板，成卷的称带钢。宽度在650mm以上的称宽带钢,不足650mm的称窄带钢。厚度4～60mm,宽度在200mm以下的热轧钢材在中国称扁钢。0.02～0.1mm的冷轧带称薄带。0.02mm以下的带材称箔材,钢铁箔材习惯称为超薄带。关于板带材的制造方法，见中、厚板轧制，带钢热轧，薄板叠轧，带钢冷轧，箔材轧制。