1) adsorption-magnetic field
吸附磁性场
3) magnetic adsorbent
磁性吸附剂
1.
A novel Fe_3O_4/acrylate-based magnetic adsorbent were prepared by suspension polymerization using divinybenzene as a crosslinker.
以二乙烯苯为交联剂,采用悬浮聚合法制备了Fe3O4/丙烯酸系磁性吸附剂。
2.
The results showed that the diameter of the magnetic adsorbent was 35~55μm and the amount of Fe3O4 was 18%.
结果表明,磁性吸附剂粒径35～55μm,Fe3O4质量分数18%,能有效吸附金属离子。
3.
The effect of magnetic fleld on magnetic adsorbent adsorbing Cu 2+ was studied through the adsorption experiment.
通过吸附实验研究磁场对磁性吸附剂吸附铜的影响，结果表明：磁化吸附剂的吸附量比不磁化大，并随磁场强度增大而增加；磁化吸附剂的吸附平衡关系式可用Ｆｒｅｕｎｄｉｌｉｃｈ吸附等温方程描述；磁性吸附剂对Ｃｕ２＋的穿透吸附量随磁场强度增大而增加，穿透吸附量（或穿透体积）还与Ｃｕ２＋液的进口浓度和流速有关。
4) magnetic biosorbent
磁性生物吸附剂
1.
Study on the adsorption property of magnetic biosorbent on Cu2+;
磁性生物吸附剂对Cu~(2+)吸附性能的研究
5) Magnetic affinity adsorbent
磁性亲和吸附剂
1.
Thus, three magnetic affinity adsorbents were prepared.
磁性琼脂糖微球经环氧氯丙烷活化后 ,分别键合 6-氨基己酸、氨基乙酸和乙二胺为间隔臂 ,用水溶性碳二亚胺为缩合剂 ,分别偶联对氨基苯甲脒、l-精氨酸甲酯和胍基己酸 ,制备了 3种磁性亲和吸附剂 ,并用于尿激酶粗品的分离纯化。
6) magnetic affinity adsorption
磁性亲和吸附
补充资料：磁性材料2．薄膜磁性材料
磁性材料2．薄膜磁性材料
Magnetie Materials 2.Thin Film
在一定外加磁场作用下，其反磁化畴(磁矩取向与外磁场方向相反的畴)变为圆柱形磁畴。从膜面上看，这些柱形畴好像浮着的一群圆泡，故称磁泡或叫泡踌(另见磁性材料2.昨晶态磁性材料)。在特定的电路图形、电流方向和一定磁场情况下，可做到控制材料中磁泡的产生、传翰和消失，实现信息的储存和逻辑运算的功能。磁泡的直径在微米量级(0 .5~5协m)，每个磁泡的迁移率在1 .26~12.6em八s·A/m)〔 102一i03cm八s·oe)〕，因而可制成存储密度为兆位/cmZ(Mbit/cmZ)和数据处理速率为兆位/s(M肠t/s)的运算器件。磁泡器件经过近20年研究和开发，已取得广泛的实际应用。 对磁泡材料的主要要求是:(l)各向异性常数凡>粤斌，磁化强度从>外磁场强度H;(2)杂质缺陷小，2一~”~’.J泌~-一‘产’~~一~一’、~尹一~~~’J”均匀性好。目前研究得比较清楚的有铁氧体单晶薄膜和稀土一过渡金属薄膜。从制备工艺和性能稳定、器件开发等情况看，以铁氧体磁泡材料比较成熟，早期是用钙钦石型铁氧体单晶片来作磁泡材料，后为YIG单晶薄膜所取代。它是用液相外延法在Gd3Ga5OI:(简称GGO)基片上生成的单晶薄膜，其厚为微米量级。表4为稀土石榴石R3FesolZ的磁性;表5为一些磁泡材料的基本特性数值。农4稀土石抽石R.Fe‘ol，的磁性┌───────────┬────┬────┬────┬────┬────┬────┬────┬────┬─────┬────┬────┐│R │Y │Sm │EU │Gd │Tb │Dy │、Ho │Er │T】11 │Yb │Lu │├───────────┼────┼────┼────┼────┼────┼────┼────┼────┼─────┼────┼────┤│补偿温度，~p，K │ 560 │ 560 │ 570 │ 290 │ 246 │ 220 │ 136 │ 84│4