您的位置:首页 -> 词典 -> 锌镁铜铬锰铁硅合金
1)  zircal
锌镁铜铬锰铁硅合金
2)  FeMnSiCrNi alloys
铁锰硅铬镍合金
3)  magnesium-manganese-zinc alloy
镁锰锌合金
4)  Cr-Mn-Cu alloy white cast iron
铬锰铜合金白口铸铁
1.
The wear resistance of Cr-Mn-Cu alloy white cast iron after heat treatment was studied and compared with that of as-cast Cr-Mn-Cu alloy white cast iron,the wear failure mechanism and microstructure on the wear end surface and nonwear end surface were analyzed.
以铬锰铜合金白口铸铁的铸态材料为对比材料,考察了热处理后的铬锰铜合金白口铸铁材料的耐磨性能,对试验材料的磨损失效机理和磨损端面与无磨损端面的金相组织进行了分析。
2.
The wearing resistance,microstructure,worn surface morphology and hardness change in wearing end-face and non-wearing end-face of Cr-Mn-Cu alloy white cast iron were tested and analyzed.
对铬锰铜合金白口铸铁的耐磨性、无磨损端面及磨损端面的微观组织、磨损形貌及硬度进行了试验和分析。
3.
The erosive-wear resistance of heat treated Cr-Mn-Cu alloy white cast iron was investigated compared with that of as-cast one, and the impact fractures,the erosive-wear resistant failure mechanism and the section metallurgical structure of the test materials were analyzed.
以铸态铬锰铜合金白口铸铁为对比材料,考察了热处理后的铬锰铜合金白口铸铁的抗冲蚀磨损性能,并对试验材料的冲击断口形貌、抗冲蚀磨损失效机理和冲蚀磨损横切面的金相组织进行了分析。
5)  ferromanganin
铁锰铜合金
6)  ferro silicon manganese alloy
硅锰铁合金
1.
Through taking on complex deoxidizing and alloying process with ferro silicon manganese alloy in EBT electric arc furnace of Shiheng special steel plant the question of accretion and poor deoxidation in liquid steel is well solved Thus smooth production of continuous casting is ensured,the billet quality is increased,the production cost is decrease
石横特殊钢厂在EBT电炉上采用硅锰铁合金复合脱氧合金化工艺,较好地解决了钢水结瘤和钢水脱氧不良的问题,确保了连铸生产顺行,提高了铸坯质量,降低了生产成本。
补充资料:镁铝锌系铸造镁合金


镁铝锌系铸造镁合金
magnesium-aluminium-zinc cast magnesium alloy series

mellUxlnx一zhuzao melhej一n镁铝锌系铸造镁合金(magnesium一alumini-um一Zine east magnesium alloy series)以铝、锌为主要合金化元素的铸造镁合金,可用于砂型和金属型铸造,也可用于压力铸造,具有良好的流动性和焊接性能,热裂倾向性低,但有较大的显微疏松倾向。 中国牌号ZM一5(7.5%一9.0%Al,0.15%一0.5%Mn,0.2%一0.8%Zn,Mg为余量)合金,ZM一10(9 .0%~1 0.2%AI,0.15%一0.5%Mn,0.2%一0.8%zn,Mg余量)合金。zM一5合金为镁铝锌系铸造镁合金的代表,相当于前苏联牌号的M月5合金。合金中杂质为铁、铜、镍、硅、钻等,根据需要可适量加些被。 铝是主要合金化元素并含有锌和锰,通过改变铝、锌含量可改变合金的力学性能、铸造性能及抗蚀性能。铝含量的增加能进一步改善合金的铸造性能和提高合金的强度,但使伸长率和抗腐蚀性能降低。加入少量的锌和锰能显著提高合金的抗蚀性能,还可以提高合金的强度。但锌含量增加会使合金的缩松倾向增加。ZM一5合金的铸态组织由固溶体叔Mg)为基体,沿它的晶界以不连续网状分布着y(Mg‘A13)相,以及分布在固溶体叔Mg)中的Mn一Ai化合物小质点所组成。热处理强化常采用两种规范:(1)淬火(T4):加热到370~380℃保温2一4h,再升温至415士5℃保温12一16h,然后在空气中冷却。(2)淬火时效(T6):淬火后再在175士5℃人工时效16h。ZM一5合金的力学性能见表1。 表1 zM一5合金的力学性能详 镁铝锌系铸造镁合金结晶间隔较大,充型能力良好,铸造工艺性能及物理常数见表2。表2 zM一s合金铸造工艺性能及物理常数}牛粉粉{字朴 镁铝锌系铸造镁合金能铸出外形和内腔形状复杂的铸件,加之镁合金在汽油、煤油、润滑油中很稳定,因而多用于航空工业的燃油系统和润滑系统。还可作为在受冲击载荷时能吸收大量能量的零部件及飞机着陆轮的轮毅。 (杨朴)