1) suppress defect
压缩缺陷
2) compression of flaw signals
缺陷信号压缩
3) back end defect
缩尾缺陷
1.
The causes of back end defects of copper alloy extruded products were analyzed, provide preventive measures, the product quality had been improved effectively, thus achieving good economic benefit.
分析了铜合金制品缩尾缺陷的产生原因,并提出了相应的预防措施。
4) shrinkage defect
收缩缺陷
1.
Solidification Simulation and Shrinkage Defect Prediction of S.G. Iron Casting in Sand Lined Metal Mold;
铁型覆砂球墨铸铁件凝固模拟及收缩缺陷预测
2.
Adopting optimizing design of risers, sound turbochargers were prepare d, and solidification process and shrinkage defects of turbocharger castings wer e analyzed.
本研究采用水冷铜坩埚真空感应凝壳技术和熔模型壳离心浇注的铸造方法制备γ-TiAl增压涡轮,通过改善冒口工艺获得了健全的γ-TiAl涡轮铸件,分析了γ-TiAl增压涡轮的凝固过程和收缩缺陷产生原因。
3.
Influence of the initial temperature fields and mold hardness on the shrinkage defect of ductile iron casting by EPC process was mainly investigated in this paper.
本文主要讨论了初始温度场和铸型硬度对消失模铸造球墨铸铁件收缩缺陷的影响。
5) glaze shrinkage freckle
缩釉缺陷
1.
After analyzing glaze shrinkage freckle on cap and pin insulator body observed in manufacturing process,the author attributes it firstly to deviation of body moisture from technological specification,and secondly to low temperature at glazing and thick ink for marking.
就悬式绝缘子在生产过程中出现的缩釉缺陷进行了分析,认为:首先是坯件入窑前水分含量达不到工艺要求,其次是上釉温度低和记号墨汁过浓。
6) extrusion defect
挤压缺陷
1.
The extrusion defects of aluminium profiles most have relation with die structure,and recommending several methods of design dies and to overcome defects of aluminium profiles.
铝型材挤压缺陷的产生很大一部分与模具结构有关,简要介绍几种型材模具的优化设计,以克服挤压型材缺陷的产生。
补充资料：点缺陷(见晶体缺陷)
点缺陷(见晶体缺陷)
point defect
点缺陷point defeet见晶体缺陷。