1.
One-bath acid dyeing and anti-crease finishing of cotton fabrics;
棉织物酸性染料染色和抗皱整理一浴法
2.
Research on the anti-crease finishing of tussah fabrics with glyoxal finishing agent;
乙二醛整理剂对柞蚕丝织物抗皱整理的研究
3.
and time in the anti-crease finishing, and the optimum process was found for ramie blended fabrics according to the strength loss and elastic recovery angles (T+W).
对影响整理效果的树脂和催化剂用量、焙烘温度和时间等因素进行了试验,以强力损失和弹性回复角(T+W)指标为依据,找出了适合苎麻棉混纺织物抗皱整理的最佳工艺:树脂NDW100g/L、催化剂MgCl220g/L、纤维保护剂SVN20g/L,焙烘温度160℃,焙烘时间控制在3min,弹性回复角(T+W)可达265°,强力损失38。
4) crease-resistant finishing
抗皱整理
1.
Nano-ZnO is used as a catalyst for crease-resistant finishing of silk fabric with water-soluble polyurethane.
将纳米 ZnO(氧化锌)作为催化剂,应用于水溶性聚氨酯对丝绸的抗皱整理。
2.
Cotton fabric was treated with the mixture of glutaraldehyde and hydrolyzed starch in the crease-resistant finishing of the fabric.
采用戊二醛与水解淀粉对棉织物进行抗皱整理,通过正交试验,讨论戊二醛和催化剂用量、淀粉水解时间、焙烘温度和焙烘时间等因素对整理后棉织物折皱回复角、断裂强力保持率、白度的影响,得出最佳工艺方案:淀粉水解时间为90min,戊二醛的浓度为70g/L,催化剂浓度为25g/L,焙烘温度为140℃,焙烘时间为3min。
3.
Nano-SiO2 was used as the catalyst of amino-silicone elastomer for crease-resistant finishing of silk knitting fabric.
用纳米SiO2作为氨基硅酮弹性体的催化剂,对真丝针织物进行抗皱整理。
5) anti-crease finish
防皱整理
1.
The anti-crease finish on cotton fabric with built finshing agnt of glyoxal and water soluble fibrion is introduced.
文章采用乙二醛和水溶性丝素溶液复配整理剂对棉织物进行防皱整理,通过L16(45)正交试验,系统分析了不同工艺条件对棉织物断裂强力、折皱回复角的影响,并得到了最佳工艺参数。
2.
Then procedures such as mercerization、 singeing、 low temperature plasma panel,biological enzyme polishing and anti-crease finish are done.
介绍了苎麻竹纤维的特点,用苎麻纱线与竹纤维纱线交织生产苎麻竹纤维织物,并对织物进行丝光、烧毛、低温等离子、生物酶抛光和防皱整理,研制的织物具有透气、挺刮、不贴身、抑菌、抗菌、易吸湿散湿、具有凉爽感和弹性感的特点,又增加了织物的悬垂感等布面光洁清晰,手感柔软,色泽鲜艳亮丽,具有丝绸般的风格。
3.
This project applied glyoxal resin to crease-resistant finishing of soybean fiber and discussed about the influence on anti-crease finishing effect of soybean fabric treated with different finishing dosage, curing temperature and time.
将乙二醛树脂用于大豆纤维织物的防皱整理 ,讨论了整理剂用量、焙烘温度、焙烘时间对抗皱整理效果的影响。
6) Wrinkle resistant finishing
抗皱整理
1.
Research on the wrinkle resistant finishing of silk fabrics with polymaleic acid;
聚马来酸对真丝织物抗皱整理研究
补充资料：酚醛烘干皱纹漆
分子式：
CAS号：
性质：以酚醛树脂为主要成膜物质的一类装饰性烘漆。由酚醛树脂、颜料、干性油、催干剂和有机溶剂制造而成。该漆烘烤后，漆膜坚硬，皱纹美观，分粗、中、细三种皱纹。适用各种仪器、仪表、文教用具、小五金零件等装饰保护，可遮蔽底材的不平整。
CAS号：
性质：以酚醛树脂为主要成膜物质的一类装饰性烘漆。由酚醛树脂、颜料、干性油、催干剂和有机溶剂制造而成。该漆烘烤后，漆膜坚硬，皱纹美观，分粗、中、细三种皱纹。适用各种仪器、仪表、文教用具、小五金零件等装饰保护，可遮蔽底材的不平整。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条