3) bending stress fatigue limit
弯曲应力疲劳极限
4) rotary bending fatigue limit
旋弯疲劳极限
5) Bending Fatigue
弯曲疲劳
1.
Effects of Drawing Velocity on Grain Growth and Bending Fatigue of CuAlNi Shape Memory Alloy with Column Crystal in Heat Mould Continuous Casting;
连铸速度对CUALNI记忆合金晶粒长大及弯曲疲劳的影响
2.
Effect of Surface Defects on Bending Fatigue Behavior of High Strength Spring Steel;
表面缺陷对高强度弹簧钢弯曲疲劳性能的影响
3.
Study on the designing method of bending fatigue in gears those bear loading on both sides;
双面受载齿轮弯曲疲劳设计方法研究
6) flexural fatigue
弯曲疲劳
1.
Influence of dosages of ground granulated blast-furnace slag and fly ash on flexural fatigue performance of concrete;
磨细矿渣和粉煤灰掺量对混凝土弯曲疲劳性能的影响
2.
Investigation flexural fatigue behavior of steel fiber reinforced concrete for pavement surface stratum under cyclic load;
循环荷载下路面用钢纤维混凝土的弯曲疲劳研究
补充资料:弯曲疲劳
分子式:
CAS号:
性质:又称屈挠疲劳。材料在交变弯曲应力作用下发生损伤乃至断裂的过程。在疲劳初期,内部结构将发生改变,接着出现疲劳裂纹的成核和扩展,当疲劳裂纹失稳扩展时就导致疲劳断裂。在作弯曲疲劳试验时,按控制变量,可分为应力疲劳和应变疲劳两类。应力疲劳时,应力幅值恒定在一较低值,加载的频率高,断裂周次也高;应变疲劳时,应力幅值恒定在较高值,加载频率低,断裂周次也低。弯曲疲劳是工程实际中经常会发生的问题,弯曲疲劳试验也是材料疲劳试验方法中比较成熟的一种方法。
CAS号:
性质:又称屈挠疲劳。材料在交变弯曲应力作用下发生损伤乃至断裂的过程。在疲劳初期,内部结构将发生改变,接着出现疲劳裂纹的成核和扩展,当疲劳裂纹失稳扩展时就导致疲劳断裂。在作弯曲疲劳试验时,按控制变量,可分为应力疲劳和应变疲劳两类。应力疲劳时,应力幅值恒定在一较低值,加载的频率高,断裂周次也高;应变疲劳时,应力幅值恒定在较高值,加载频率低,断裂周次也低。弯曲疲劳是工程实际中经常会发生的问题,弯曲疲劳试验也是材料疲劳试验方法中比较成熟的一种方法。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。